重要的是，国产服装作本质阻燃织物，如尼龙或聚酯。
It's important that homemade costumes be made of inherently flame-resistant fabrics, such as nylon or polyester.
并对阻燃织物的阻燃性能进行了测试证明该阻燃织物整理工艺是可行的。
The flame retardant performances of this fabric is also tested. It prove that the flame retardant processing is practicable and successful.
结果表明，溶胶-凝胶法红磷微胶囊整理的棉织物具有良好的阻燃效果和耐久性，但白度和断裂强力有一定程度的下降。
Results showed that the treated cotton fabric had good flame retardancy and durability, but its whiteness and tensile strength decreased to some extent.
用扫描电镜法对整理后的织物表征，并测定整理后棉织物的阻燃性能和耐久性。
Treated cotton fabric was characterized by scanning electron microscopy, and their flame retardancy and durability were tested.
这是一种高密织物，是阻燃防护服的理想面料。
这些方法能改善织物的折皱和收缩倾向并且具有阻燃保护功能。
The methods described serve to improve the creasing and shrinkage tendency of the fabrics and to provide a flame retardant protective function.
该织物应该由100%阻燃聚酯纤维制成。
The fabric shall be made of 100 per cent flame retardant polyester fibre.
本文具体叙述阻燃涤纶ATY汽车用内饰织物的工艺设计，重点是提出LT102型剑杆织机的织造参数。
This paper relates the technology design of fire proofing polyester ATY for car decorative fabric. The weaving parameters of LT102 tyre rapier loom are introduced.
本机主要适用于多层光边织物的织造，特别适用于织造4层6 - 8级煤矿井下及码头阻燃输送带整体带芯。
This machine is mainly applicable to weave multi-layer true selvedge fabrics, especially to weave 4 layers grade 6-8 integral core for fire retardant conveyor used in the coal mine or at the wharf.
开发自身具有阻燃性的纤维，然后制成织物。
Inherently flame resistant fibers may be developed and converted into cloth.
本发 明的金属包覆织物至少在单面上具有由不使用含卤化合物或锑化合物制备的阻燃剂组合物构成的层。
The metal-coated fabric has, on at least one side thereof, a layer made of a flame retardant composition prepared without using any halogenated compound or antimony compound.
文章介绍了棉织物传统的阻燃方法与新型的阻燃方法，以及纳米技术在阻燃整理中的应用，并针对新型阻燃技术的发展前景进行了展望。
The traditional and new ways, as well as nanometer technology, used in processing cotton flame-retardant fabric are introduced. The development of new flame-retardant technology is prospected.
产品包括：钢丝绳芯输送带、整芯阻燃输送带、织物帆布芯输送带和特种输送带等四大系列输送带产品。
Products include: steel cord conveyor belt, the whole core conveyor belt fire-retardant fabric and special canvas core conveyor belt conveyor belt conveyor belt products, such as the four series.
采用PANOF转杯纱开发的织物在阻燃性、耐磨性方面明显优于环锭纱织物。
The flame retardant fabric developed with rotor spun PANOF yarns was obviously superior to that with ring spun yarns.
并合理预测了常规阻燃纤维、阻燃剂和织物阻燃整理方法的发展趋势。
Therefore, development prospect of conventional fire-retardant fibers, fire retardant and fire proofing methods are forecasted reasonably.
1998年建成首条塑料面织物整芯阻燃输送带生产线；
Completed in 1998 the first plastic surface the whole fabric core conveyor belt production line of flame retardant;
这种织物应用范围广泛，它采用阻燃材料，有些织物采用了完全新颖的组织和结构，这些措施都使织物适合贴身穿着。
This involved the use of flame retardant materials, some in completely new structures and constructions, which are suitable for textiles worn next to the body.
文章介绍了纯棉织物耐久性阻燃整理的生产工艺，针对生产中影响阻燃整理效果的关键环节，提出了相应的预防和解决措施。
The durable flame-retardant finishing was introduced for all cotton fabric. The author also proposed the prevention steps against the key causes affecting the finish result.
阐述了亚麻的阻燃机理，采用FK- 103对亚麻织物进行阻燃整理，能赋予整理织物优良的阻燃效果且成本较低。
This paper describes the mechanism of the flame retardant for linen, using FK-103 as flame retardant finishing textile.
交融的元aramydic以及准aramydic纤维布局，Carmyth织物具备比种族以往任何用于创作发明耐磨材质高阻燃性。
Blending a mix of meta-aramydic and para-aramydic fibers, Carmyth fabric has a higher flame resistance than any previous material used in the manufacturing of race wear.
尼龙66织物被广泛应用于军用和民用服装，但其燃烧时产生的熔滴是尼龙织物阻燃的难题。
Nylon-66 fabric have been widely used in military and civilian clothing, however, the melting drip from burning nylon-66 fabric is still a problem need to be solved.
提出以羟甲基改性尼龙- 6织物与反应型有机磷系、溴系阻燃剂进行耐久性阻燃整理的新方法。
A new technique for the durable flame retarding treatment of hydroxymethyl nylon 6 textiles with reactive flame retardants is put forward.
研究了一种用耐高温的玻璃纤维织物与阻燃的棉织物层压而成的新型热防护复合织物。
A novel thermal protective fabric is studied, which is a composite product by laminating a kind of high temperature resistant glass fibre fabric and a flame retardant cotton cloth.
论述芳砜纶织物以聚氨酯涂层实现防水透湿及阻燃功能的方法。
This article discussed the method how to coat the polyurethane coating agent on PSA fabric to obtain the waterproof, moisture permeable and flame-retardant properties.
实验证明，此法研制的涂层织物可以达到抗浸服标准所要求的防水透湿及阻燃性。
The experiment results indicated that those properties of the coated fabric can reach the requirement of the standard GJB2320 basically.
本文简要介绍了三种阻燃抗静电织物的研制方法，分别是阻燃和抗静电功能整理法；
This article introduces three methods developing double-functional fabric with flame-retardant and antistatic.
一方面要研究各类纤维、织物的燃烧理论，还要研究阻燃剂在纤维上的阻燃机理。
The theory must be studied about all kinds of fibres and fabric, and about burning preventing agents, and about the mechanism of burning prevention.
增加了新的织物阻燃性测试步骤。
New flammability testing procedures for fabrics have been added.
这是一种高密织物，是阻燃防护服的理想面料。
It is a perfect facing material of flame retardant protective clothing.
还可以被应用于纸张、纤维织物、装饰板、地板革、壁纸、地毯、陶瓷釉料、杀菌剂，涂料的生产中，以提高阻燃性能。
Also can be used for paper, fabric, decorative plates, leather floors, wallpaper, carpet, ceramic glaze, fungicide, dope processing. to improve the fire-retardant capability.