采用交流阻抗法研究硫化矿碳糊电极体系在氯化钠电解液中的界面动力学行为。
The interface dynamic behaviors of sulfide mineral carbon paste electrodes in NaCl electrolyte were investigated by alternating current impedance technique.
同时，采用电化学阻抗等测试技术，研究了碳钢在SRB腐蚀过程中生物膜结构与腐蚀行为关系。
The relation of the structure of biofilms and corrosion behavior of SRB on carbon steel was also investigated using electrochemical impedance spectroscopy (EIS).
采用电化学动电位扫描和交流阻抗研究了铜在模拟斯德哥尔摩雨水中的腐蚀行为。
Corrosion behavior of copper in a simulated rainwater of Stockholm area was studied by electrochemical impedance spectrum and polarization curves.
提出了钽的氧化反应式及反应控制步骤；得出其氧化膜电容量随着氧化电位的增加而减少，阻抗与阳极极化行为存在相关关系。
The results shows the capacity of the anode oxidation membrane decreases with the increasing of oxidation potential, and there exists relationship between impedance and behavior anode polarization.
采用阳极极化和电化学阻抗谱（EIS）技术研究了AZ31镁合金的电化学腐蚀行为。
The electrochemical behavior of AZ31 Mg alloy was investigated by measuring anodic polarization curves and electrochemical impedance spectroscopy(EIS).
得出其氧化膜电容量随着氧化电位的增加而减少，阻抗与阳极极化行为存在相关关系。
The results shows the capacity of the anode oxidation membrane decreases with the increasing of oxidation potential, and there exists relationship between impedance and behavior anode polarization.
应用电化学阻抗谱和氯离子探针技术，研究在氯化物侵蚀作用下混凝土中钢筋的腐蚀行为。
Electrochemical impedance spectroscopy and chloride sensor were employed to study the corrosion behavior of reinforcing steel in concrete.
利用循环伏安、恒电位阶跃、电化学阻抗等电化学测试技术研究了电结晶初期以及电沉积过程的电化学行为。
The electrodeposited behaviours in the initial stage and deposited process were investigated by cyclic voltammetry(CV), chronoamperometry(CA), electrochemical impedance spectroscopy(EIS).
电流控制电流源（CCCS）存在不同支路电流之间的控制行为，给该类网络节点阻抗矩阵的形成带来困难。
The current of current-controlled current source (CCCS) branch is controlled by the current of another branch, which makes it difficult to build the node impedances matrix (Z-matrix).
精神分析理论、行为主义、人本主义和认知心理学对阻抗有着不同的解释。
There are different explanations about resistance coming from psychoanalysis, behaviorism, humanism and cognitive psychology.
采用电化学阻抗法研究支撑液膜膜液的流失行为，并采用等效电路法分析得到的交流阻抗图谱。
The losing behavior of liquid in supported liquid membranes (SLMs) was studied by electrochemical impedance spectroscopy (EIS) method in this paper.
采用交流阻抗技术研究了带锈铁器在模拟海水介质中的电化学行为。
Electrochemical impedance technique is employed to study the corrosion of the simulated rusted cast iron in seawater.
这一结果提示我们，在对高中生进行心理咨询时，如果运用行为疗法，要注意采取一定的措施，避免可能出现的心理阻抗。
This phenomenon informs us that when using behavior therapy on high school students in counseling, we should take some measures to avoid possible psychological reactance;
运用交流阻抗(EIS)法和单线性扫描(lsv)法研究X70钢在乳酸溶液中的腐蚀行为，乳酸浓度和温度对X70钢腐蚀行为的影响。
Corrosion behavior of X70 steel in lactic acid solutions with different concentration and different temperature was investigated by means of EIS and Linear Sweep Voltammetry (LSV).
用电化学阻抗谱研究了丙烯酸系乳胶作为混凝土添加剂或钢筋表面涂层时对钢筋腐蚀行为的影响。
Acrylic emulsion was introduced into steel reinforcing concrete as concrete admixtures or rebar coatings in order to prevent steel reinforcements from corrosion.
高压电缆的金属护套交叉互联导致行波在多个波阻抗不连续点产生了复杂的折反射行为，这对高压电缆线路的行波故障测距产生很大的影响。
The reflection and refraction of traveling wave are quite complicated at the sheath-crossing point of high voltage power cable, due to its remarkably noncontinuous surge impedance.
这种影响称为“阻抗resistance”(佛洛德)，或“防御defensiveness”(罗杰斯)，或“安全操作security operation”(沙利文)，以及用来解释大量的行为。
This influence is termed "resistance" (Freud), or "defensiveness" (Rogers), or "security operation" (Sullivan), and a great deal of behavior is thereby explainable.
采用交流阻抗技术研究了带锈铁器在模拟海水介质中的电化学行为。
Potential attenuation behavior of rusty cast iron with thick rust scale after suspending cathodic protection (CP) in 3.
利用极化曲线技术、电化学阻抗测试技术等方法，研究了氯离子含量对黄壤土中碳钢腐蚀行为的影响。
The effects of chloride ion on corrosion of carbon steel in yellow soil were studied by using polarization curve technique, electrochemical impedance spectroscopy(EIS).
以锌盐、葡萄糖酸盐为主要缓蚀成分复配的适用于天然海水中碳钢的高效缓蚀剂，采用极化曲线、循环伏安曲线和交流阻抗谱图分析了该缓蚀剂的阳极脱附行为。
The adsorption and anodic dis-adsorption action of corrosion inhibitors for carbon steel in natural seawater was studied by electrochemical methods such as polarization, cycle polarization, and EIS.
以锌盐、葡萄糖酸盐为主要缓蚀成分复配的适用于天然海水中碳钢的高效缓蚀剂，采用极化曲线、循环伏安曲线和交流阻抗谱图分析了该缓蚀剂的阳极脱附行为。
The adsorption and anodic dis-adsorption action of corrosion inhibitors for carbon steel in natural seawater was studied by electrochemical methods such as polarization, cycle polarization, and EIS.
应用推荐