分析了铸铁五金件表面存在的缺陷及其对镀锌层质量的影响。
The defects of surface of cast iron hardware and its influence on the quality of zinc deposit were analyzed.
在不同的工作锥角度下,比较镀锌钢丝拉拔后的抗拉强度、锌层质量、模子寿命。
The tensile strength, zinc coat mass and service life of die of galvanized steel wire after drawing are compared on the condition of different work cone angle.
阐述了机械镀锌层的表面质量、结合力及其耐蚀性,提出了机械镀锌的沉积过程模型。通过实验数据及分析加以验证。
Surface quality adhesion to substrate and corrosion resistance of zinc coating of mechanical plating are described. The deposition model is proposed and is confirmed by experimental results.
实践证明,采用恰当的工艺控制方法,可有利于提高机械镀锌层的质量,提高镀锌层的机械性能。
The practice proved that, using the appropriate Craft control method, is advantageous in enhancing the Coating quality and the Mechanical property.
本文研究了X-射线荧光法测定镀锌板表面铬层质量的分析方法,实验选择了仪器的最佳测定条件和参数,并对方法的精密度和准确度进行了考查。
Determining of the surface chromium content on Salvanized Sheet Steel by X ray fluorescence method was introduced, and selected the best determining condition and parameter of the instrument.
在不同的工作锥角度下,比较镀锌钢丝拉拔后的抗拉强度、锌层质量、模子寿命。
To set forth the effect by such factors as speed of taking up, temperature of galvanizing pot, dipping time, raw material on Zn-coat mass of steel wire galvanizing by dipping.
镀锌钢因其良好的抗腐蚀性能而广泛应用于各个领域,而镀锌层的存在使得镀锌钢的焊接过程和焊接质量受到不利影响。
Galvanized steel is widely used in industry due to its excellent corrosion resistance. However, the zinc coating greatly reduces the welding process property of galvanized steel.
镀锌钢因其良好的抗腐蚀性能而广泛应用于各个领域,而镀锌层的存在使得镀锌钢的焊接过程和焊接质量受到不利影响。
Galvanized steel is widely used in industry due to its excellent corrosion resistance. However, the zinc coating greatly reduces the welding process property of galvanized steel.