碱性镀锌镀层起泡的原因很多，实际电镀中需要有针对性地排除故障。
There are so many reasons for blistering, so the trouble-shooting must be promoted pertinently to the corresponding reasons.
减少施镀时间，降低镀层厚度，解决了镀层起泡脱皮质量问题，保证了化学镀镍零件的防腐性能。
Reducing plating time and coating thickness can solve these problems. So these methods can solve quality problem of the bubbling and...
本文对多层陶瓷外壳电镀层起泡的成因进行了探讨和分析。在实际工作的基础上，提出了解决起泡应采取的措施。
The reasons of plating layer blister on multilayer ceramic package are analyzed. On the base of practice the resolve methods are indicated.
化学镀镍层起泡脱皮会导致无镀层部位的加速腐蚀，在表面处理中是不允许出现的。
Bubbling and peeling on chemical nickel coating cause fast erosion of no coating part. The appearance can't emerge in the surface treatment.
化学镀镍层起泡脱皮会导致无镀层部位的加速腐蚀，在表面处理中是不允许出现的。
Bubbling and peeling on chemical nickel coating cause fast erosion of no coating part.
化学镀镍层起泡脱皮会导致无镀层部位的加速腐蚀，在表面处理中是不允许出现的。
Bubbling and peeling on chemical nickel coating cause fast erosion of no coating part.