制取铝稀土合金系列的新思想和新工艺过程；
Some New ideas and new process in preparation of Al-RE alloys series.
本文总结了铝镁系合金添加稀土元素的试验研究，提供了有关的性能数据。
This paper is a summary on the experimental investigation of Al-Mg alloys with the alloying addition of RE.
高尔凡钢丝，低碳钢丝的镀锌层是合金，合金成分5%铝-混合微量稀土合金锌层。
Galfan wire, galvanized low carbon steel wire is 5% aluminum alloy, the alloy composition mixed trace rare earth zinc alloy layer.
高尔凡(锌铝合金)，又分为锌- 5%铝-混合稀土合金钢丝和锌- 10% -铝混合稀土合金钢丝。
Gao Erfan (zinc aluminum alloy), and divided into zinc -5% aluminum alloy steel wire and zinc alloy -10% - mixed rare earth alloy steel wire.
采用磷、硫、稀土、锶、钠、碳等进行双重细化变质处理过共晶铝硅合金已取得了良好的效果。
The good effect has been gained on the hypereutectic Al Si alloys treated with some double refining and modifying agents such as P, S, RE, Sr, Na, C, etc.
总结了碳钢和不锈钢以及铝、锌、铜、镁等金属及其合金稀土钝化处理的国内外研究状况。
The research status worldwide of rare earth passivation treatment of carbon steel and stainless steel, aluminum, zinc, copper, magnesium and its alloy were summarized.
亚共晶铝硅合金的变质元素除钠以外，还有锶、碲、钡、锑、钾、稀土、硼、硫等。其中，应用较多的是含钠和锶的变质剂。
The modifying elements used in hypoeutectic Al Si alloys, besides Na, there are also Sr, Te, Ba, Sb, K, RE, B, S, etc.
本文研究工业纯铝中含RE（混合轻稀土，含量为0～0.275％）时对7075合金组织和性能的影响。
The effects of RE (mixed light RE, 0—0.275%) content in commercial pure aluminium on the structure and characteristics of 7075 alloy are investigated in this paper.
这样的分为两种材质，锌- 5%铝-混合稀土合金钢丝、锌- 10%铝混合稀土合金钢丝。
This is divided into two kinds of materials, zinc -5% aluminum mixed rare earth alloy steel wire, zinc -10% aluminum mixed rare earth alloy steel wire.
本文叙述了阳极氧化工艺对稀土铝锰合金电解着色膜物理化学性能的影响。
The influence of technology of anodic oxidation on the physicochemical properties of rare earth Al-Mn alloy electrolytic coloured membrane is recited.
研究了涡轮叶片材料M38G合金渗稀土-铝涂层的工艺过程和组织结构。
The RE-aluminizing technique and coating structure of gas turbine blade made of alloy M38G are studied.
通过对不同变质剂加入量下共晶硅形貌的观察及特定部位的微区成份分析，探讨了稀土变质铝硅合金的机制。
The modifying mechanism was researched by viewing the morphology of the silicon with different amount of modifier and making microanalysis on the particular region of the ahoy .
在泡沫铝和泡沫铝合金中添加适量稀土元素，可以提高泡沫铝和泡沫铝合金的耐腐蚀性能；
When the addition amount of rare earth elements was appropriate, the corrosion resistance of aluminum and aluminum alloy foam was improved.
研究了稀土元素铈对铝锂合金表面贫化层的影响以及表面贫化层对合金腐蚀形态的影响。
The influence of cerium on depletion layer of the surface of al Li alloys and the influence of the depletion layer on the corrosion morphology of the alloys were studied.
从热力学分析了用铝、钙、硅、钛及铁铬铝中的铝还原稀土氧化物成稀土金属进入合金的可能性。
The possibility of reduction of rare-earth oxides to metals by aluminum in Fe-Cr-Al alloys as well as by aluminum, calcium, silicon and titanium has been studied from the view point of thermodynamics.
本文介绍了稀土铝基轴承合金的研制，合金包铝及复合轧制工艺。
The aluminium base bearing alloy with rare earths is studied in this paper, which recommends making alloy, coating aluminium and rolling technology of bimetal.
稀土铝合金因有上述的特点，而广泛地应用在电工铝的生产上。
As such characteristics above, Al-RE alloy is applied to aluminumelectroconductor widely.
随着稀土元素加入量的增加 ，可以显著提高铝、镁合金的综合性能特别是高温力学性能。
The addition of more RE elements can significantly enhance the comprehensive properties, especially mechanical behavior at high temperature.
稀土元素作为微量元素加入铝、镁合金中，可以净化合金熔体，细化、变质微观组织，减少夹杂。
The addition of rare earth (re) as trace elements to aluminum or magnesium alloys can purify the melts, refine and modify the microstructure, reduce the inclusion.
这样的分为两种材质，锌- 5%铝-混合稀土合金钢丝、锌- 10%铝混合稀土合金钢丝。
This is divided into two kinds of material, aluminum zinc - 5% - mixed rare earth alloy steel wire, aluminum zinc - 10% mixed rare earth alloy steel wire.
添加稀土元素之后 ，镁铝锌合金的铸态组织得到细化 ，并在显微组织中形成铝的稀土相 ；
The whole as cast microstructures of the alloy were refined and RE containing Al phase was formed with RE addition. The ageing peak value was slightly raised.
添加稀土元素之后 ，镁铝锌合金的铸态组织得到细化 ，并在显微组织中形成铝的稀土相 ；
The whole as cast microstructures of the alloy were refined and RE containing Al phase was formed with RE addition. The ageing peak value was slightly raised.