结果显示，采用有机保护层的焊接界面金属间化合物层厚度明显超过了浸银层；
The thickness of intermetallic compounds (IMC) layer with OSP was higher than that of I-Ag.
结果表明：J55和N80钢热浸镀铝后的镀层组织均可分为纯铝层和铁铝金属间化合物层两层；
The results showed that the hot-dip aluminizing coatings on both the J55 and N80 steels were composed of aluminum layer and Fe-Al intermetallic compound layer.
采用过渡层法进行钛合金与不锈钢的焊接时，基本能够避免焊接材料之间脆性金属间化合物的大量生成，从而有效提高焊接接头的连接强度。
The intermetallics could be avoided effectively by using the method of transition layers between titanium alloy and stainless steel, and the tensile strength of welded joints is enhanced.
通过低压铸造后固溶处理的方法，获得了网状金属间化合物增强铝合金表面复合层。
Intermetallic compound foam reinforced aluminium alloy surface composite layer are obtained by solution treatment after low pressure Casting.
回顾了十年来受主金属氯化物石墨层间化合物在零磁场下传导性能的实验工作。
Experimental data in zero-field of the metal chloride acceptor GICs of the last decade was reviewed.
回顾了十年来受主金属氯化物石墨层间化合物在零磁场下传导性能的实验工作。
Experimental data in zero-field of the metal chloride acceptor GICs of the last decade was reviewed.