这种合金是用两种金属熔合而成的。
这种金属是用其他两种金属熔合而成的。
This metal is formed by the fusion of two other types of metal.
轧入金属异物。扎入金属表面、一般不与金属熔合的外来金属异物。
Rolled-In Slugs. A foreign metallic body rolled into the metal surface, usually not fused.
我没预见到近期会有大笔开支,除非他们发明了一种我负担得起的技术,把我的骨骼和亚德曼金属熔合在一起,就像金刚狼那样。
I see no large upcoming expenditures, unless they develop an affordable technology to fuse my skeleton with Adamantium like Wolverine.
折叠。经过轧制或采用其它方式加工的金属沿着轧制金属表面折叠起来,但并未被熔合成完好金属。
Lap. Fold of metal which has been rolled or otherwise worked against the surface of rolled metal, but has not fused into sound metal.
被压实的材料置于炉内烧结,在高温下炉内环境可控,金属粉末熔合形成固体。
This compacted material is placed in an oven and sintered in a controlled atmosphere at high temperatures and the metal powders coalesce and form a solid.
的过程中,被称为添加剂制造,允许金属的粉末形式可以熔融,然后熔合在一起成为使用激光的对象。
The process, known as additive manufacturing, allows the powder form of metals to be melted and then fused together into objects using a laser.
碳扩散的结果是在紧邻熔合界面的焊缝金属一侧形成高硬度的增碳层,母材金属一侧产生硬度较低的贫碳层。
Carbon migration induces the formation of carbon-enriched layer in the austenitic weld metal and carbon-denuded layer in the Cr-Mo steels base metals.
她喜欢看似电线熔合而成的金属的家具腿。
She liked metal furniture legs that looked like wires fused together.
辊芯熔合界面附近的外层金属先后经历了凝固、熔化、再凝固的过程。
Outer cladding metal nearby the fusion interface of roll mandrel experienced the process of solidification-fusion-re-solidification.
X65管线钢在焊接过程中,内侧焊缝金属出现横向和纵向沿熔合线方向的裂纹,横向裂纹贯穿焊缝金属横截面。
The longitudinal cracks along bond line and the transverse cracks which cut across the weld metal cross section inside weld metal were formed, while X65 pipe line steel was welding.
对涂层-金属基体界面区的激光熔合工艺、熔合区的组织结构、元素分布进行了研究。
It has been investigated to the laser melting process and the merging parts microstructure and the elements distribution of coating-metallic substrates interface zone.
焊接接头的拉伸试验断裂部位在焊缝。焊接HAZ熔合线附近的硬度值最高,远离熔合线硬度降低,并逐渐接近母材金属的硬度。
The tensile test fracture area locates on weld seam, and the hardness near HAZ fusion line is the highest, away from the fusion line, the hardness declines and reach the parent metal hardness.
焊接接头的拉伸试验断裂部位在焊缝。焊接HAZ熔合线附近的硬度值最高,远离熔合线硬度降低,并逐渐接近母材金属的硬度。
The tensile test fracture area locates on weld seam, and the hardness near HAZ fusion line is the highest, away from the fusion line, the hardness declines and reach the parent metal hardness.