对接枝母体胶料和丙烯酸单体进行了选择。
Selection of master rubber and acrylic monomer was described.
本文研究了木素磺酸盐和丙烯酸单体的接枝共聚机理。
The graft mechanism of lignosulfonate and acrylic acid was studied in this paper.
报道了将丙烯酸单体接枝到合成橡胶上的接枝共聚方法。
A newly developed grafting copolymer of synthetic rubber with acrylic monomer has been reported.
以过硫酸铵为引发剂，在超声波辅助下引发丙烯酸单体聚合。
Under ultrasonic polyacrylic acid was synthesized with ammonium persulfate as initiator.
阐述了丙烯酸单体用氧化-还原引发体系进行的“还原聚合’。
The paper presented a reductive polymerization or acrylic acid that can be performed with redox system.
红外光谱分析表明，甲基丙烯酸单体在聚丙烯大分子链的叔碳原子上发生接枝共聚。
IR analysis shows that graft copolymerization takes place on the tertiary carbon atom of PP molecular chain.
将液态含氟丙烯酸单体与丙烯酸酯类单体采用常压溶液聚合工艺，合成了支链含氟的丙烯酸树脂。
A branched fluorine - containing acrylic resin has been developed through solution polymerization at normal pressure with liquid fluorine - containing acrylic acid monomer and acrylate monomers.
硅丙烯酸树脂是由硅树脂和丙烯酸单体反应而得到的产品，或是硅树脂和丙烯酸类聚合物的共混物。
Silicone acrylic resins can be either the reaction product of a silicone intermediate with acrylic monomers, or a cold blend of silicone resin and acrylic polymers.
由于其脆性及混溶性差，用柔软的丙烯酸单体改性，可制得物理机械性能和外观优良的防腐蚀涂料。
Because of its brittleness and poor compatibility, it has been modified with a soft acrylic monomer to form a corrosion protective coatings with excellent mechanical properties and appearance.
通过上述方法可将具有巨大分子结构的二酚单体与二元酸单体聚合，得到高耐热且透明的聚酯材料。
By adopting the method, the diphenol monomers with a macromolecular structure can be polymerized with the binary acid monomer to obtain the highly heat-resistant and transparent polyester material.
发明的两性离子共聚物是由从对羧酸质子内部转移到丙烯酰胺或丙烯酸单体氨基酸组的三元共聚物。
The zwitterion terpolymers of the invention are made from the terpolymers by internal transfer of the proton of the carboxylic acid to the amino group of the acrylamide or acrylate monomer.
这些材料包括各种丙烯酸单体和低聚物、伯胺、仲胺和叔胺、酸官能单体和低聚物、硅酮、蜡和弹性体等。
These materials include a variety of acrylic monomers and oligomers, primary, secondary and tertiary amines, acid-functional monomers and oligomers, silicones, waxes and elastomers, among others.
制备了一种以聚丙二醇增韧改性的环氧树脂为母体，接枝丙烯酸单体所形成主体树脂，经离子化反应得到阴极电泳涂料。
A cathodic electrodeposition coatings was prepared employing a polypropylene glycol toughness-enhanced epoxy resin as matrix and acrylic monomers as grafted copolymer.
Quintana - Murci博士的数据来自人类基因组单体型计划图，旨在对单核苷酸多态性，即SNPs进行归类。
Dr Quintana-Murci's data were drawn from a project called HapMap, which catalogues what are known as single-nucleotide polymorphisms, or SNPs.
这样一种方法对于制备双官能单体和合成己二酸的中间体特别有用。
Such a process is particularly useful in the production of difunctional monomers and intermediates in the synthesis of adipic acid.
研究无机填料、功能单体及牙齿表面酸蚀与否等因素对单组分可见光固化齿科正畸粘接剂剪切强度的影响。
The influence of inorganic filler, functional monomer, etching treatment of teeth surface, etc on the shearing strength of one-component visible-light curing orthodontic adhesive was studied.
发现前后两次滴加的单体比例、酸浓度以及酸种类是主要影响因素。
It has been found that the rat IO of monomers in two separated charging and varieties and concentration of acids are the main influencing factors.
增大单体的浓度和加入少量无机酸也能提高接枝率。
The grafting was also enhanced by raising concentration of monomers and by acid as well.
通过调整丙烯酸组分的单体组成和涂料配方，研制出一种耐候性的IPN改性丙烯酸聚氨酯涂料。
A weather resistant IPN-improved acrylic polyurethane coating has been developed by controlling the composition of acrylic prepolymer and coating formulation.
讨论了交联单体及酸的用量对性能的影响。
The affection of the quantity of the linking monomer and acid to its performance was discussed.
本研究采用丙烯酸酯单体聚合制成一种全新的合成冷封胶。介绍了制备方法和有关性能。
The preparation process and the related properties of the cold-seal adhesive polymerized from acrylate monomers were included in the paper.
以丙烯酸酯类为单体，采用复合乳化剂研制了自交联无纺布胶粘剂。
Self crosslinking adhesive for non woven fabrics with acrylates monomers and compound emulsifier is prepared.
寻找一种第二单体与丙烯酸酯共聚。
引入活性单体和丙烯酸酯来改善聚合物的增稠性能和抗电解质性能。
Active monomer and acrylic esters were introduced to improve the thickening property and electrolyte resistance.
将这些单体与丙烯酸丁酯共聚得到了三种乳液聚合型品红成色剂。
Three latex magenta couplers were formed by emulsion copolymerization of these monomers and butyl acrylate.
本文探讨了丙烯酸系单体接枝聚丙烯非织造布的接技工艺。
The grafting technology of acrylic acid monomer grafting polypropylene nonwoven fabric is explored.
以最常见的两种单体甲基丙烯酸甲酯和苯乙烯为例。
Take the most widely used monomers, styrene and methyl methacrylate as an example.
配方：溶剂：醋酸，单体中甲基丙烯酸甲酯体积分数为10%到30%。
The recipe: acetic acid as solvent, MMA contents from 10 vol % to 30 vol %.
配方：溶剂：醋酸，单体中甲基丙烯酸甲酯体积分数为10%到30%。
The recipe: acetic acid as solvent, MMA contents from 10 vol % to 30 vol %.