等离子表面淬火硬化层的硬度分布,在某一区域内无明显的硬度梯度,这与常规淬火方法的结果不太一样。
The hardness distribution without obviously declining gradient in one range of the hardened layer produced by plasma quenching is rather different from that by conventional quenching.
硬化层深度是等离子弧表面淬火效果的重要指标之一,而硬化层深度与工艺参数、淬火过程中温度场的变化密切相关。
Hardening depth related to the technical parameters and the quenching temperature field is an important target by plasma surface quenching.