晶粒长大、晶界面积减少以及镀层表面生成较厚的、致密的氧化膜是耐蚀性提高的主要原因。
The main cause of better corrosion resistance was due to growth of granules, decrease of grain boundary area, and formation of thick and compact oxidation film on the coating surface.