以硅烷偶联剂KH550为桥梁,利用酰胺化反应将改性的HBPE(记做MHBPE)接枝到超细二氧化钛表面。
By use of silane coupling agent KH550 the modified HBPE (MHBPE) was grafted onto the surface of ultrafine titanium dioxide by amidation reaction.
XRD分析表明分子筛在杂化材料中保持原状,FT - IR证实TDI能够与沸石分子筛表面的硅羟基进行接枝反应。
The XRD shows that zeolite without changing in the hybrid materials. The FTIR proves that the grafting reaction can happen between TDI and Si-OH in the surface of the zeolites.
同时丝素蛋白膜用氨气等离子体处理后在表面接入氨基,利用1,3丙磺酸内酯与氨基的反应在材料表面接枝磺酸基团。
Meanwhile, functional groups were also introduced by the reaction of 1,3 propane sultone with amine sites on the surface of silk fibroin film which were produced by NH 3 gas plasma.
通过紫外光引发甲基丙烯酸甲酯的接枝聚合,在聚丙烯膜表面引入了反应性基团酯基。
The surface of polypropylene microporous membranes was activated by the graft polymerization of methyl methacrylate initiated with ultraviolet-photo.
用对二氯甲基苯作为后交联剂,与聚丙烯接枝苯乙烯-二乙烯苯纤维进行后交联反应,制备出具有高比表面积的后交联纤维。
The post-crosslinking fiber was prepared by cross-linking PP-ST-DVB fiber with p-xylylenedichloride according to the friedel-crafts reaction and was given a series of synthesis tests.
采用一步法和二步法研究了聚乙烯薄膜表面的N- 乙烯基吡咯烷酮光接枝反应,并用傅立叶变换红外光谱仪定性表征了反应结果。
The photografting polymerization of Nvinyl pyrrolidone (NVP) on the surface of LDPE film with photo grafting method was studied and LDPEgNVP was characterized by FTIR qualitatively.
高分子膜表面在紫外光辐照下可能发生光接枝反应,从而使高分子膜的表面性质发生很大的变化。
Polymer membrane surface may occur grafting reaction by the UV-irradiation, so that the properties of membrane surface could change a lot.
高分子膜表面在紫外光辐照下可能发生光接枝反应,从而使高分子膜的表面性质发生很大的变化。
Polymer membrane surface may occur grafting reaction by the UV-irradiation, so that the properties of membrane surface could change a lot.