文章综述了国内外有关螺旋焊缝管的断裂试验和研究工作的概况。
The article is a general review of the test and research work on fracture in relation to spiral welded pipes at home and abroad.
采用纵剪带钢生产小口径螺旋焊管时,超声波检验经常在焊缝的一侧发现缺陷波,而X射线拍片检验却很难发现。
The defects will be found in the seam side with ultrasonic inspection but hardly found with X ray inspection as the small diameter spiral pipe production with the split strip steel.
介绍了在螺旋焊缝汇管上焊接支管时的防变形措施、焊接方法和检验结果。
This paper introduces the measure, welding method and inspection result to prevent the welding deformation formation of spiral-seam pipe header after tapping.
介绍了螺旋埋弧焊管焊缝余高的重要性、焊缝余高对焊缝力学性能的影响以及余高对螺旋埋弧焊管防腐的影响。
This article introduced weld reinforcement importance to SSAW pipe, effect of weld reinforcement to weld mechanical property and to SSAW pipe anti-corrosion.
失效分析结果表明,螺旋焊管焊缝断裂主要是由于管道附近泥浆化趋势、较高的堆土以及焊缝缺陷造成。
The results showed that the failure of spiral welding pipes was mainly caused by piled solid, the increase of the water in solid and th...
失效分析结果表明,螺旋焊管焊缝断裂主要是由于管道附近泥浆化趋势、较高的堆土以及焊缝缺陷造成。
The results showed that the failure of spiral welding pipes was mainly caused by piled solid, the increase of the water in solid and th...