本系统利用硅晶胞的动态移动描述整个硅衬底腐蚀模拟的全过程，需要的存储空间小，提高了模拟计算的速度。
Because of the combined of static and dynamic storage structure, the speed of the simulation is improved, so that the PC can carry out this etching simulation.
采用SEBF重腐蚀防护技术的船用水泵，在公司内的试验台架上进行模拟海水的对比试验。
Contrast test simulating seawater has been performed on Marine pumps using SEBF sever corrosion prevention technology on the test bench in the Company.
本文介绍传感器微机械加工中使用的各向异性腐蚀的计算机模拟。
This paper introduces the computer simulation for the anisotropic etching used in micro-machining of sensors.
通过室内模拟试验和现场取样测试的方式，对比研究应力腐蚀条件下影响锚杆使用寿命的因素。
The influencing factors on the durableness of anchor with stress corrosion by the way of simulation in laboratory and site sampling are studied.
采用电化学动电位扫描和交流阻抗研究了铜在模拟斯德哥尔摩雨水中的腐蚀行为。
Corrosion behavior of copper in a simulated rainwater of Stockholm area was studied by electrochemical impedance spectrum and polarization curves.
随着模拟降雨强度的增大，A 3钢的腐蚀速率和冲刷量增大。
The corrosion rate and runoff quantity of A3 steel increase with intensity of simulated rain increasing.
本文利用收集气体、测定腐蚀电流和模拟电池放电等方法来选择和检验缓蚀剂。
Corrosion inhibitors were selected and tested by method of collected gas, corrosion current measurement and simulated battery discharge.
针对混凝土硫酸杆菌腐蚀的研究方法分为细菌模拟测试和现场暴露测试。
The research of thiobacillus corrosion on concrete can be roughly divided into two groups: bacteria simulation tests and exposure tests in situ.
本文将利用计算机辅助设计(CAD)技术实现腐蚀过程的模拟。
In the paper, computer aided design (CAD) technology is used to achieve simulation of sacrificial layer etching.
在模拟溶液中，电化学反应非常容易进行，腐蚀速率很高。
In simulated soil solution, electrochemical reactions are easiest to take place, so the corrosion rate is the highest.
采用失重法和电化学方法对铜在模拟苦咸水溶液中的腐蚀电化学行为进行了研究。
The electrochemical behaviors of copper in the simulating bitter and brackish solution was studied using weight method and electrochemical techniques.
针对不同的涂层体系，通过模拟其在不同腐蚀环境中的失效过程，获得大量的电化学交流阻抗测试数据。
By simulating the failure process of coating in different corrosion environment, a large number of electrochemical impedance test data has been collected.
本文通过机械加工模拟腐蚀件的实验，对红外热图像处理中的四种典型算法进行了研究。
Four typical algorithms used in infrared image processing are studied in the simulation experiment of machined corrosion parts.
通过模拟闭塞腐蚀电池试验研究了钢在热处理前后的点蚀扩展速度，并利用电子探针和扫描电镜分析了钢表面的蚀坑形貌。
The pitting propagation rate was evaluated by simulating occluded corrosion cell (SOCC), and corrosive characteristic of pits was studied by scanning electro microscopy (SEM) and EPMA.
建立了一套磁阻探针大气腐蚀检测系统，实现了模拟大气环境下金属腐蚀速率的快速检测。
An atmospheric corrosion measurement system of reluctance probe is established to realize quick measurement of metal corrosion in different simulated atmospheric conditions.
基于以上的观点，本文采用慢应变速率实验方法探讨了预形变对X70管线钢在模拟土壤介质中应力腐蚀敏感性的影响。
On the base of above appoints, the slow strain rate test was used to study the effect of prestraining on the SCC susceptibility of X70 pipeline steel in simulate soil media.
采用模拟和加速腐蚀试验方法，研究了广州地铁工程混凝土对地下水的耐腐蚀性能。
The corrosion resistance of Guangzhou Metro engineering concrete to groundwater was investigated by simulated and accelerated corrosion tests.
提出了几种土壤宏电池腐蚀的室内模拟试验方法，实验表明，金属在土壤中的宏电池腐蚀作用确实相当严重。
Some indoor simulation testing methods were used to study the behavior and mechanism of macrocell corrosion in soil. Serious macrocell corrosion of metals was found.
采用浸泡、电化学、模拟试验以及拉伸试验对冷轧厂电镀锌机组不锈钢紧固螺栓在现行工艺条件下遭受严重腐蚀进行了研究。
The severe corrosion of stainless steel fastening bolts on Electrolytic Galvanizing Line(EGL)in cold strip mill plant under current working conditions has been studied.
选择两种具有不同类型硫化物夹杂的碳钢，通过模拟蚀孔的闭塞腐蚀电池试验，研究了它们在人工海水中的孔蚀扩展行为。
Using OCC simulation test, behavior of pitting propagation of two carbon steels for shipbuilding with different sulfide inclusions in synthetic seawater was studied.
计算结果同时也表明，对于表面覆盖有钝化膜的材料的数值模拟，建立合理的流动腐蚀动力学模型是数值计算方法应用成功与否的关键。
The modeled results also show that the ability to simulate corrosion of materials with surface passive film to some extent depends on their corrosion kinetics process tested by experiments.
进行了模拟原电池试验和预蠕变试样的应力腐蚀试验。
Simulated galvanic cell tests and stress corrosion tests using pre-creeping specimens were conducted.
本文介绍了矿用玻璃纤维网假顶材料在模拟自然工况和特殊工况条件下的恒温、静态耐腐蚀试验及结果。
The constant temperature, static state corrosion resistant test and results of mining glass fibre net false roof materials under analog working conditions and special working conditions are presented.
模拟实际工程中不同金属连接形式和不同的环境介质，对其进行腐蚀现象和腐蚀程度的长期观察，得到各种工况腐蚀程度图。
Through the simulation of different metal connecting forms and different environment medium in practical construction, long-term observation of corrosion phenomena and degree has been done.
用高能激光束和电子束轰击实验材料，模拟聚变堆面对等离子体材料在等离子体破裂时的工作状态，考察了4种掺杂石墨材料在热冲击下的热腐蚀规律。
The thermal shock behavior of 4 kinds of impurity doped graphites was investigated under a simulated plasma disruption condition using high-energy laser and electron beam.
模拟研究了井下环境N 80钢在油田采出液(主要是CO2水溶液)中的静态和动态腐蚀行为。
It is an analog study of static and dynamic analog study of corrosion action of N80 steel in the extraction liquid (mainly CO2 water solution) of oil field under condition of well.
在含有不同浓度HCO3-的库尔勒模拟溶液中对X70钢楔形缝隙模拟构型进行缝隙腐蚀实验。
The crevice corrosion behavior of X70 steel was studied in the Ku'erle simulated solution of various HCO3- concentrations by using a wedge-shaped crevice model.
通过现场腐蚀挂片、室内模拟实验和电化学测量研究了A3钢在富营养化淡水环境中和洁净淡水环境中的腐蚀行为及影响因素。
The corrosion behaviors of A3 steel in eutrophic water and clean water were studied by locale corrosion specimen and experiments in simulant condition.
通过现场腐蚀挂片、室内模拟实验和电化学测量研究了A3钢在富营养化淡水环境中和洁净淡水环境中的腐蚀行为及影响因素。
The corrosion behaviors of A3 steel in eutrophic water and clean water were studied by locale corrosion specimen and experiments in simulant condition.
应用推荐