研究了正火处理对FAS390Q桥壳钢显微组织、强度、冲击韧性和韧脆转变温度的影响。
The effect of normalizing on microstructure, strength, impact toughness and ductile-brittle transition temperature of FAS390Q axle housing steel was studied.
结果表明，本钢X70管线钢具有高强度、高抗动态撕裂能力、高低温冲击韧性以及低韧脆转变温度。
The results indicate that the X70 pipeline steel with acicular ferrite microstructure has high strength, high toughness, low transition temperature and high dynamic tear-resistance.
对试验钢筋的应变时效敏感性、韧脆转变温度、可焊性、强度与韧性的配合进行了系统的测试和研究。
The sensibility of strain aging, ductile-brittle transit temperature, weldability, and the coordination between strength and ductility of reinforced steel bars were systematically investigated.
对于脆性较大的UPR，只有在采用加载速度较慢的断裂韧性来表征其韧性时，方能观察到这一脆韧转变现象。
For the UPR with greater brittleness, the brittle-tough transition was observed only when the toughness of the resin was characterized by fracture toughness at a slower loading rate.
研究了磷含量和晶粒尺寸对低碳钢的屈服强度、 冲击韧性和韧脆转变温度的影响。
The influence of phosphorus and grain size on yield strength and Charp V-notch toughness of low carbon steels have been investigated.
有魏氏组织的试样较呈等轴铁素体的试样有更高的冲击韧性和更低的韧脆转变温度。
The specimens with Widmanstatten structure have higher impact strength and lower ductile-brittle transition temperature than those with equiaxial granular ferrite structure.
有魏氏组织的试样较呈等轴铁素体的试样有更高的冲击韧性和更低的韧脆转变温度。
The specimens with Widmanstatten structure have higher impact strength and lower ductile-brittle transition temperature than those with equiaxial granular ferrite structure.