模拟油在岩心中的自发乳化驱采收率和总采收率分别为24.5%和71.8%，与超低界面张力聚合物表面活性剂驱相近。
The simulated oil spontaneous emulsification flooding recovery and total recovery with cores are enhanced by 24.5% and 71.8%.
表面有机化改性是提高木质填料（木纤维或木粉）的分散程度和增强其与聚合物基体界面相互作用的重要手段。
Surface organic modification plays an important role in improving wood fillers (xylon and wood flour) dispersion and enhancing the interfacial interactions between the wood fillers and polymer matrix.
采用硅烷偶联剂对无机填料和石棉纤维进行表面处理，提高无机填料与聚合物基体的界面相互作用；
The results show that after being treated with coupling agent, interface interaction between inorganic fillers or asbestos fiber and epoxy resin enhances quite a little.
结果发现由于颗粒填料表面和环氧基体的相互作用，从填料表面开始形成了一层致密的聚合物界面层。
It was found that a dense polymeric interface layer would be formed on the surface of solid fillers due to the interaction between paniculate filler surface and epoxy matrix.
水分的出现会加速木塑复合材料制品表面老化褪色、弯曲性能损失以及聚合物和木粉界面相容性的破坏等。
The presence of water accelerated aging properties, such as changes of color and flexural property and interfacial compatibility of wood flour and polymer.
由于是硬壳包装，电极表面聚合物膜在溶胀时体积增大，可在电极和隔离膜间形成良好的界面。
Volumes of the polymer films on the surfaces of the electrodes are increased when in swelling due to crust packaging, and a good interface is formed between the electrodes and the separation films.
由于是硬壳包装，电极表面聚合物膜在溶胀时体积增大，可在电极和隔离膜间形成良好的界面。
Volumes of the polymer films on the surfaces of the electrodes are increased when in swelling due to crust packaging, and a good interface is formed between the electrodes and the separation films.