并且与加入未处理碳纳米管、处理后碳纳米管的聚乙烯醇薄膜在力学与电学性能方面进行了研究。
The electrical and mechanical properties of the films were compared with those containing untreated or treated CNTs.
使用新合成的氧化偶氮染料对定向和拉伸的聚乙烯醇薄膜染色，制备了具有较高偏振度和耐高温高湿性能的偏振片。
The polarizer having high polarizing activities and durability to heat and moisture was prepared by dipping the newly synthesized azoxy dye into oriented and stretched polyvinyl alcohol film.
从聚合物结构方面分析了聚乙烯醇(pva)薄膜的水溶性，提出用共混改性方法提高PVA薄膜的溶解性能。
The water-solubility of poly (vinyl alcohol) (PVA) films is analyzed from the polymer structure, the blend modification method is put forward to increase the water solubility of PVA films.
采用表面涂覆法，将聚乙烯醇（PVA）薄膜固定在聚丙烯无纺布表面，进行表面亲水改性。
The hydrophilic modification of polypropylene non-woven fabric (NWF) surface was conducted by coating PVA (poly vinyl alcohol) film on the NWF surface via dip-coating method.
该薄膜卷通过用聚乙烯醇树脂溶液成型薄膜、然后将该薄膜卷绕到芯管上而制得。
The film coil can be obtained by forming the film from the polyvinyl alcohol resin solution, and coiling the film onto the core tube.
聚乙烯醇(PVA)薄膜在水溶性、可降解性等方面的独特优点使其成为当前研究的热点。
PVA film is known as a popular research direction because of its special excellent characteristics in many aspects, e. g. water solubility and degradability.
采用表面涂覆法，将聚乙烯醇(PVA)薄膜固定在聚丙烯无纺布表面，进行表面亲水改性。
The surface modification of polypropylene non-woven fabric (NWF) by PVA (polyvinyl alcohol) was researched by dip-coating of PVA to immobilize PVA on the NWF surface.
结果表明，在薄膜玻璃面一侧，聚乙烯醇浓度高于纤维素，而在乙醇而一侧则无组分浓度的差异。
The results showed that the PVA is richer than CELL at the glass-side surface of the blend films, whereas, on selectivity is detected at the ethanol-side...
结果表明，在薄膜玻璃面一侧，聚乙烯醇浓度高于纤维素，而在乙醇而一侧则无组分浓度的差异。
The results showed that the PVA is richer than CELL at the glass-side surface of the blend films, whereas, on selectivity is detected at the ethanol-side...