耐火喷涂料属不定形耐火材料,具有独特的成型方法和施工工艺,在工业炉窑上有着广泛的使用价值。
The refractory coat-injecting materials belong to monolithic refractories and have a special forming process and construction techniques, and could be widely applied in industrial furnaces.
分析了加热炉水冷梁外层耐火材料损毁机理,研制了新型耐火喷涂料,确定了水冷梁用半干法喷涂料的配方。
The damage mechanism of outer refractory in water-Cooling beam of heating furnace is analysed. The new spraying coating is researched and the formulation of spraying coating is confirmed.
适应喷涂材料:乳胶漆、真石漆、浮雕效果涂料、防水材料、耐火材料等。
To adapt spraying material:latex paint, powder paint, the effect of relief coatings, waterproofing materials, refractories, and so on.
如按iso 834曲线升温,耐火性能达到3h,一般涂料涂层厚度约需20 ~30mm;由于涂层较厚,需要多次喷涂,施工困难。
E. g. by ISO 834 curve thawing, fireproof performance reach 3h, general coating thickness need about 20 ~ 30 mm, Due to the coating thicker, requiring multiple coating, construction difficulties.
如按iso 834曲线升温,耐火性能达到3h,一般涂料涂层厚度约需20 ~30mm;由于涂层较厚,需要多次喷涂,施工困难。
E. g. by ISO 834 curve thawing, fireproof performance reach 3h, general coating thickness need about 20 ~ 30 mm, Due to the coating thicker, requiring multiple coating, construction difficulties.