还探讨了升温速率对结晶熔融行为的影响。
This peper also studied the effect of DSC scanning rates on the crystallize and melting behavior.
实验结果表明该偶联剂界面层的形成对PPS/PES共混物的熔融、结晶行为以及抗冲击性能具有深刻的影响。
Theformation of this interphase had strong effect on the melting and crystallization behaviour of PPS/PES blend, and the impact strength of PPS/PESblend was raised.
由实验和观察结果可以看出,熔融凝固过程的微观分析有助于揭示保护渣在结晶器内的行为。
From the experiment and the observation, it is found that microscopic analysis in melting and solidification process can greatly help to reveal the behaviour of powder in the mould.
结果表明,加工历史对尼龙的结晶和熔融行为影响很大。
The results showed that the processing history had a great influence on the crystallization and melt behavior of nylons.
采用差示扫描量热仪(DSC)研究了离聚物苯乙烯-丙烯酸钠对聚对苯二甲酸乙二酯(PET)的结晶行为及熔融行为的影响。
The effect of ionomer styrene-sodium acrylate(SAA-Na) on the crystallization and melting behaviors of polyethylene terephthalate(PET) was investigated by using differential scanning calorimetry(DSC).
采用DSC,WAXD研究了在超临界CO2作用下,温度、压力和共溶剂对双酚A型聚碳酸酯(BAPC)的结晶和熔融行为的影响。
The influences of temperature, pressure and cosolvent on the melting behavior of BAPC treated by supercritical CO2 were studied by DSC and WAXD.
对复合体系的形态结构、熔融及非等温结晶行为进行了研究。
The morphological structures and melting properties as well as non-isothermal crystallization behavior of blend were investigated.
用DSC研究了两种成核剂成核PP的非等温结晶行为与熔融特性。
The non isothermal crystallization behavior and melting characteristics of polypropylene(PP) nucleated by different nucleating agents were studied by DSC.
通过DSC方法研究了蒙脱土对尼龙66熔融与结晶行为的影响,探讨了蒙脱土对尼龙66结晶的成核作用。
The influence of montmorillonite(Mont. ) on melting and crystallization behavior of nylon 66 has been investigated by DSC.
研究了沉积在熔融玻璃表面的金原子的扩散、凝聚以及结晶行为。
The diffusion, aggregation and crystallization characteristics of gold atoms deposited on molten glass surfaces are studied.
应用dsc、TGA和TMA研究了固相聚合pet树脂的双重熔融行为、热稳定性及瓶坯、包装瓶的结晶性能和膨胀性。
The double - melt behavior, thermal stability of soild state condensation polymerization of PET and the crystallization, expansibility of PET bottle have been studied by DSC, TGA and TMA.
通过DSC研究了氯化聚乙烯的熔融行为,观察到氯化聚乙烯存在结晶和共结晶;
The melting behavior was also studied by DSC. Crystalline and cocrystalline was found.
通过DSC研究了氯化聚乙烯的熔融行为,观察到氯化聚乙烯存在结晶和共结晶;
The melting behavior was also studied by DSC. Crystalline and cocrystalline was found.