结果表明，较低的铁素体轧制温度和较高的铁素体区压下量时，IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
The results showed that the if steel has better deep drawability, higher mechanical and texture strength and elongation if the hot rolling temperature was low with big reduction in ferrite region.
if钢的冷轧压下率分配对深冲性能有重要的影响，是由于冷轧过程的压下率对(111)织构的形成有影响。
The reduction partition has effect important in two-time cold rolling on Drawability of IF steel, because reduction has effect in cold rolling on {111} texture.
强流脉冲电子束轰击可以实现316L不锈钢表层的选择性净化，表面织构化及表面快速钛合金化，从而提高不锈钢的耐蚀性。
The main results are summarized as follows:1, HCPEB bombardment induces the selective purification on the top surface of 316L stainless steel, surface texturation and rapid surface alloying with Ti.
尝试了小形变量轧制对立方织构电工钢织构形成的影响。
Effects of temper rolling on the cubic texture formation in primary recrystallized electrical steel were investigated.
通过铁素体区热轧工艺生产elc钢的工业试验，研究了一种ELC钢的热轧组织、织构及性能。
The hot rolled steel microstructure, texture and properties of an ELC steel was conducted to study through ELC steel hot rolled in ferrite region process industrial production experiment.
通过铁素体区热轧工艺生产ELC钢的工业试验，研究了一种ELC钢的热轧组织，织构及性能。
The hot rolled microstructure, texture and properties of an ELC steel hot rolled in ferrite region, cold rolled and annealed were studied.
利用EBSD技术研究了不同热轧温度下436不锈钢热轧织构的变化规律和显微组织特征。
The evolution of microstructure and texture characteristic of 436 ferritic stainless steel sheets, which were hot rolled under different rolling temperatures by EBSD technology, was investigated.
结果表明，较低的铁素体轧制温度和较高的铁素体区压下量时，IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
The relationship of deep-drawing property and rolling parameters of IF steel was researched by the testing of ferritic rolling and annealing.
结果表明，较低的铁素体轧制温度和较高的铁素体区压下量时，IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
The relationship of deep-drawing property and rolling parameters of IF steel was researched by the testing of ferritic rolling and annealing.