实验结果表明，当芳纶短切纤维与芳纶浆粕的配比为1：1.5左右时，所抄造纸页的抗张强度、撕裂度、匀度最好；
The experimental results show that when the matching between Aramid fiber and PPTA is 1:1.5 more or less, the tensile strength, tear and formation of aramid paper is the best.
用甘油作为塑化剂，将糊化淀粉和溶胀纤维按不同配比进行熔融共混来制备完全可生物降解塑料。
Full-biodegradable plastics were prepared by means of melt blending of paste starch with swelled fiber at different blending ratio, with glycerol as plasticizer.
通过不同的木纤维和海泡石的配比进行镀层试验，对滤芯进行绝对过滤精度和压差试验，证明了这种滤芯具有良好的过滤效果。
This article has obtained excellent properties by dressing experiment with different proportion of wood fibre and sepiolite and experiment of pressure losing and absolute filtration precision.
研究中结合规范与经验，通过正交试验找到了符合惠州地区特点的较优路面纤维混凝土配比。
Through orthogonal experiment the good ratio of fiber-concrete suited for the concrete pavement in Huizhou city considering the standard and experience.
条件下测定了6种不同配比复合纤维增强阻尼混凝土的损耗因子与储存模量，最后对纤维的阻尼增强机理进行了初步探讨。
Thirdly, the loss tangent and storage modulus for fiber reinforced concretes of 6 different ratios were measured in the range of.
在纤维缠绕压力容器设计中，纤维缠绕的方向及各方向纤维用量配比是关键问题。
In design of composite pressure vessels, the fiber orientations and quantities of fiber in different orientations are the key problems.
通过正交试验对低掺量聚丙烯纤维混凝土强度因素影响作了分析，并得到了优化的试验配比。
Through orthogonal experiment the suitable ratio polypropylene fiber concrete with low content was found, and the paper analyses influencing factor on strength.
特定的配比和工艺条件下制成的碳纤维增强水泥（CFRC）试件具有压力电阻率的敏感性。
Carbon fiber reinforced cement(CFRC)specimens made under particular mix ratio and technology condition possess the stressresistivity sensitivity.
选择磁粉和聚丙烯的合理配比，既可以提高磁性纤维的纺丝性能、拉伸性能和热性能，又可以提高磁性纤维的磁粉含量。
The reasonable ratio of magnetic particle and polypropylene not only guarantees the properties of magnetic fiber but also maximizes the magnetic particle content.
得出了一种固定孔隙的制样方法，用此制样方法可观察到滤毡截面的真实形貌，从而有效地分析滤毡中粗细纤维的配比和各层的孔隙率。
The method of sample preparation by pore fixing was described. The results showed that it was a good method for studying irregular porous structure and the related ratio of felt.
从纤维素分解菌与联合固氮菌的接种配比，研究了混合培养对滤纸分解的影响。
The effect of cellulose-decomposing fungus(CDF) mixed with associative nitrogen-fixing bacterium(ANFB) to cellulose-decomposing has been studied.
以慈竹为材料，研究不同浓度和配比的GA3和IAA对综纤维和叶绿素含量动态积累的调控效应，为纸浆用竹的遗传改良研究提供理论依据。
The effects of GA3 and IAA with different concentrations and combinations on the dynamic accumulation of holocellulose and chlorophyl content in Neosinocalamus affinis were studied.
方法采用正交设计方法，确定生物粘附材料羟丙甲纤维素、卡波姆的用量及配比与制剂体外释放度及粘附力的关系。
Method Orthogonal design is used to determine the relation of the amount as well as proportion of hydroxypropyl methylcellulose and Carbopol with in vitro release and adhesive force of the tablets.
方法采用正交设计方法，确定生物粘附材料羟丙甲纤维素、卡波姆的用量及配比与制剂体外释放度及粘附力的关系。
Method Orthogonal design is used to determine the relation of the amount as well as proportion of hydroxypropyl methylcellulose and Carbopol with in vitro release and adhesive force of the tablets.