介绍了两种常用的纤维接触角测定方法。
Two common measuring methods of fiber contact Angle were introduced in this paper.
针对改性处理后的碳纤维的表面性能，进行X射线光电子能谱和单纤维接触角测试。
In addition, the surface properties of modified carbon fibers were characterized by X-ray photoelectron spectroscopy (XPS) and single fiber contact Angle test.
通过DSC、DMA、X -衍射和SEM分析纤维的结构，测试了纤维接触角、断裂强度和层间剪切强度。
The structure of treated fiber is analyzed by DSC, DMA, X-diffraction and SEM.
结果表明，经过氧化和氨化方法处理后碳纤维与环氧树脂的接触角降低。
As a result, the contact Angle of CFs with respect to epoxy resin was found to be remarkably decreased.
通过比较分析得出了等离子体处理后丙纶纤维的表面形态和表面接触角的关系。
The relationship between the morphology and the dynamic contact Angle of polypropylene fibers treated by plasma was found out through comparative analysis.
本文利用各种样品的表面张力和接触角的实验数据，说明羧甲基纤维素钠对洗涤作用的影响。
The article has accounted what Sodium Carboxy Methylcelluos effect to washing action by Samples' experimental datas of surface tension and contact Angle.
接触角的变小，说明纤维的浸润性能得到明显的改善。
The result shows that the impregnation properties of the fiber are greatly improved when the contact Angle reduces.
用扫描电子显微镜和视频变焦显微镜观察了改性烟用聚丙烯纤维的形态结构，用纤维表面动态张力仪测定了其对水的接触角。
The morphological structure was observed by scanning electron microscope and video-zoom microscope, and the contact angle to water was determined by dynamic tension meter.
本文应用单丝接触角测定仪测定了不同偶联剂处理的玻璃纤维临界表面张力。
Monofilament contact Angle meter has been used to measure the critical surface tension of glass fiber treated by different coupling agents.
纤维回用对化学热磨机械浆液体吸收性能的影响较小，即使经过五次回用，其表观动态接触角和液体吸收时间的变化也较小。
The effect of fiber recycling on the apparent dynamic contact angle and liquid absorption time of chemimechanical pulp changed little even after 5 times fiber recycling.
本文通过单纤维拔出实验、XPS、SEM、接触角测算等研究了表面改性的作用机理。
The mechanism of the surface change, as is reported in this paper, has been studied by the pull-out test, XPS, SEM, contact angle measurements.
本文研究了A 15 1偶联剂对苎麻落麻纤维与UP的接触角、纤维的吸水性、纤维表面状态及单丝强度的影响。
The influence of coupling treatment by A-151 silane coupling agent on the contact Angle between the noil ramie and up, absorptivity, filament strength and surface state of the noil ramie is studied.
主要目的是确定不同的漂白方法对硫酸盐针叶木浆纤维表面特性的影响，包括老化前和老化后。通过测量水中的动态接触角(D CA)和浆中纤维的电子光谱来检测。
The aim of this study was to determine the influence of different bleaching sequences on the fibre surface properties of softwood kraft pulp before and after ageing.
主要目的是确定不同的漂白方法对硫酸盐针叶木浆纤维表面特性的影响，包括老化前和老化后。通过测量水中的动态接触角(D CA)和浆中纤维的电子光谱来检测。
The aim of this study was to determine the influence of different bleaching sequences on the fibre surface properties of softwood kraft pulp before and after ageing.