• 结果表明,82B盘条主要原因夹杂物级别超标组织出现网状碳化物索氏体含量偏低以及盘条表面缺陷等。

    The results show that 82b wire rod brittle fracture is mainly caused by excessive inclusion, reticulate carbide, lower sorbite in the microstructure, and surface defect of wire rod.

    youdao

  • 结果表明回火索氏最佳组织形态;微观硬度均匀显著影响表面加工质量

    The results indicated that the tempered sorbite was the optimum microstructure, the inhomogeneous distribution of micro hardness affected markedly the finish quality of the steel surface.

    youdao

  • 随着温度降低,热轧材组织得到细化索氏含量提高

    With the decrease of finishing rolling temperature, the grain size is refined apparently and the contents of sorbite is increased.

    youdao

  • 研究表明碳素钢应力钢丝采用淬火取代铅浴进行索氏体化处理可行

    Effects of cold drawing and water quench process on mechanical properties of prestressed wires have been studied in laboratory.

    youdao

  • 结果表明,随轧制道增加晶粒尺寸逐渐减小索氏含量不断增加,屈服强度逐渐提高

    The results indicate that, with the increase of rolling times, the grain size becomes smaller, the content of sorbite multiplicates, and the yield strength improves.

    youdao

  • 结果表明,随轧制道增加晶粒尺寸逐渐减小索氏含量不断增加,屈服强度逐渐提高

    The results indicate that, with the increase of rolling times, the grain size becomes smaller, the content of sorbite multiplicates, and the yield strength improves.

    youdao

$firstVoiceSent
- 来自原声例句
小调查
请问您想要如何调整此模块?

感谢您的反馈,我们会尽快进行适当修改!
进来说说原因吧 确定
小调查
请问您想要如何调整此模块?

感谢您的反馈,我们会尽快进行适当修改!
进来说说原因吧 确定