尖晶石相和其中的铁空位浓度随组成和烧结温度而变化。
The ferric vacancy concentration varies with composition and heating temperature.
文章认为材料的气敏性因铁空位而产生,并随铁空位浓度增加灵敏度上升。
The gas sensitivity can be improved by the increment of the ferric vacancy concentration.
结果表明,该合金经急冷处理后由于过饱和固溶铬含量的增加,导致空位浓度显著提高与空位盘的产生。
Results show that the supersaturated solidification Cr-content increases in the rapidly quenched alloys induced the great increase of vacancy density and production of vacancy plates.
本文在考虑空位浓度对空位迁移能的影响和双空位效应的情况下,给出了体心立方金属中空位流与空位浓度梯度之间的定量关系。
The vacancy-concentration effect on the vacancy-migration-energy and the behaviour of divacancies were considered Using a formula derived for the vacancy current in BCC metals.
所有公式使用条件与高斯扩散模型相同,可用于直接求取任意浓度等值线精确的时、空位置及其特征点位置。
This modeling system has the same conditions as Gaussian diffusion model, and can calculate any concentration isoline's rigor time space location and specific points location.
氧化物磁性半导体薄膜的电输 运性质只与材料中氧空位的浓度相关。
Electric transport property of oxide magnetic semiconductor film is only related to concentration of oxygen vacancy in material.
随辐照剂量的增大,单空位、双空位和位错浓度增加,空位团的尺度和浓度都随之增大。
The concentrations of the mono-and di-vacancies and dislocations and both the concentration and size of the vacancy clusters or voids all increase with the increasing of the irradiation dose.
绿峰强度的不同取决于其结构中不同浓度的单离子氧空位。
The difference in green emission intensity results from the different level of oxygen vacancies in ZnO structures.
这应部分地与固体化学所描述的Y3 +掺杂所造成固定、额外并且是高浓度的氧空位有关。
This might partly be relative with the fixed, extra and highly concentrated oxygen vacancies resulted from Y3 + doping, the mechanics of which were as described in the solid state chemistry.
所有公式使用条件与高斯扩散模型相同,可用于直接求取任意浓度等值线精确的时、空位置及其特征点位置。
This modeling system has the same conditions as Gaussian diffusion model, and can calculate any concentration isoline's rigor Tim...
氧空位、缺陷缔合和固深度均对样品的质子电导率与掺杂浓度有一定影响。
The non-linear relationship between proton conductivity and Y3+ content of sample is closely related with the oxygen vacancy, the defect association and the solid solubility of Y.
实验结果表明随辐照剂量的增加双空位缺陷的浓度并不会无限地增加;
The results show that the intensity of V_2 is not infinitely increased with the increasing of the neutron dose.
实验结果表明随辐照剂量的增加双空位缺陷的浓度并不会无限地增加;
The results show that the intensity of V_2 is not infinitely increased with the increasing of the neutron dose.