研究表明：硼共晶组织经淬火后，具有优良的抗磨粒磨损性能。
Study shows that quenched boron eutectic structure possesses the excellent wear abrasion property.
本文论述了不同碳含量碳素钢的组织形态与抗冲击磨粒磨损性能的关系。
This paper deals with the relation of the microstructure morphology of carbon steels to its impact abrasion resistance.
结果表明：氧气流量、燃气流量和喷涂距离对涂层磨粒磨损性能具有交互影响。
It is shown that the flows of both propane and oxygen and spray distance have an interaction on the abrasive wear performance of the coatings.
利用单摆划痕法的冲击加载特性，研究了N i - P化学镀层的冲击磨粒磨损性能。
Impact abrasive wear behavior of electroless Ni-P coating was researched by means of single-pass pendulum scratching test characterized by impact loading.
配制四种不同的胶粘涂层，通过改变磨料的粒度和磨损行程对其进行磨粒磨损性能测试。
In this paper, four kinds of epoxy bond coating were obtained, the character of grain abrasion with alter particle's size and wear distance were researched.
当w（WC）大于50%时，WC的加入使喷熔工艺性能变得极差，喷熔层的硬度和耐低应力磨粒磨损性能降低。
When WC content is more then 50%, spray-fusing technological property becomes worse, hardness of sprayed coating and low-stress abrasive particle wear resistance are weaken.
笔者对磨辊表面进行激光束淬火处理，以提高磨辊的表面硬度，增强磨辊的抗磨粒磨损性能，从而达到延寿的目的。
Author used laser beam to quench the surface of the ore milling roller, so that increase its surface hardness and improve its wear resistance properties, and prolong its service life.
结果表明，无论是试验过程中的载荷、滑动速度，还是材料本身的硬度都将影响材料的磨损性能，在该试验过程中材料磨损的机制以粘着磨损和磨粒磨损为主。
The results indicate that the wear properties are influenced by load, glide velocity and rigidity, and the main wear mechanism is adherence wear and abrasive wear.
结果表明，无论是试验过程中的载荷、滑动速度，还是材料本身的硬度都将影响材料的磨损性能，在该试验过程中材料磨损的机制以粘着磨损和磨粒磨损为主。
The results indicate that the wear properties are influenced by load, glide velocity and rigidity, and the main wear mechanism is adherence wear and abrasive wear.