利用球盘磨损试验机和电化学综合测试仪研究了IBED膜层的摩擦学性能和电化学腐蚀特性。
The wear resistance and electrochemical corrosion properties of IBED coatings were investigated with ball-on-disk wear tester and electrochemical equipment, respectively.
在改进的MLD - 10型冲击腐蚀磨损试验机上，选择三种不同的冲击功，对以锰代镍的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
Under three different impact energy, LCHA with Mn in place of Ni were tested with a modified MLD-10 wear tester to investigate their behavior of corrosive impact abrasion.
在改进的MLD - 10型冲击腐蚀磨损试验机上，对不同成分的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
LCHA with several variations of composition were tested with a modified MLD-10 wear tester to investigate their behavior under corrosive impact abrasion.
结果表明，在相同试验条件下低碳高合金钢的冲击腐蚀磨损性能要优于高锰钢的。
The results show that the resistance of low carbon high alloy steel is better than that of the high manganese steel under the same test condition.
通过自制的冲击腐蚀磨损试验机，施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
电磨损分断对比试验发现，与常规机械混粉同类触头相比该材料的耐电腐蚀性能提高了40%以上。
The experimental results indicated that the arc erosion resistance of the newly developed Ag5wt%C material was more than 40% higher than that of the conventionally blended counterpart.
用环块磨损试验机进行了磨损试验，并进行了腐蚀试验。
The wear tests with ring on block wear test machine and corrosion tests were carried out.
用环块磨损试验机进行了磨损试验，并进行了腐蚀试验。
The wear tests with ring on block wear test machine and corrosion tests were carried out.