该文研究了氯丁橡胶用快速硫化体系。
The vulcanization accelerator system for neoprene is studied in this paper.
研究了硫化体系、橡塑比对共混物性能的影响。
The effects of the curing system and the amount of POM on properties of NBR/POM blends were studied.
研究了炭黑填充丁基橡胶硫黄硫化体系的硫化特性。
The vulcanizing properties of CB filled IIR with sulfur curing system were researched.
结果表明：有效和平衡硫化体系的抗硫化返原性最好；
The results showed: CV had the seriousest cure reversion , while the EV and EC has the best reversion resistance.
结果表明，该硫化体系对MTBN的交联反应是有效的。
The results show that this crosslinking system is effective for the crosslinking of MTBN.
研究了均匀实验设计法在CM过氧化物硫化体系研究中的应用。
This article was about the application of uniform design method to study of CM peroxide curing system.
氧化锌和硫黄硫化体系不能有效地将阻尼温域向高温方向拓展。
Neither zinc oxide nor sulfur vulcanization system would shift the damping temperature range upwards effectively.
过氧化物硫化体系中加入硬脂酸锌对CM起到较好的稳定作用；
Zinc stearate plays a part in stabilization of CM in the peroxide system.
本文主要研究论述硫化体系对硫化硅橡胶老化后撕裂强度的影响。
In this paper, research on curing system of vulcanized silicone rubber aging tear strength after impact.
本文主要研究论述硫化体系对硫化硅橡胶老化后撕裂强度的影响。
The effects of beating and pressing on the tearing strength of paper also have been investigated.
研究不同硫化体系对NBR/氯化聚醚（PCMO）共混物性能的影响。
The effect of different curing systems on the properties of NBR/PCMO blend was investigated.
在硫化体系不变的情况下，可用硫化曲线定性比较并用胶的共硫化程度。
When the formulation of blend was unchanged, the curing curve could be used to compare the co-vulcanization qualitatively.
对不同硫化体系和硫化方式硫化的nr胶乳胶膜的结构与性能进行研究。
The structure and property of the NR latex film vulcanized with different curing systems and curing methods were investigated.
选用硫磺硫化体系，用动态硫化法制备PVC/PNBR 热塑性弹性体。
PVC/PNBR TPE was prepared by the method of dynamic curing and the vulcanization system of sulphur.
有效硫化体系的断裂伸长率、拉伸强度、撕裂强度、耐磨性、抗热氧老化性能最好。
The elongation at break, tensile strength and tearing strength of the HVSSBR cured with EV system are the best.
结果表明，胶料需采用过氧化物硫化体系和助交联剂，用高温硫化和二次硫化工艺。
The results showed that the compound needed to use peroxide vulcanization system and aid cross-linker with high temperature cure and secondary cure process.
并用硫化体系可以改善硅橡胶硫化胶的某些性能，保持在二段硫化后不变色或少变色。
Some properties of silicone vulcanizate was improved by using this system, keeping non colour or little colour after post cure.
通过主体材料的选择、硫化体系的配合试验及防老体系的优化确定了氯丁橡胶胶料配方。
The new formulation was constituted by comparing major material, testing of various curing system and anti-aging system.
探讨发泡剂和硫黄硫化体系对NR/SBR并用海绵胶硫化发泡特性和物理性能的影响。
The effect of the blowing agent and curing system on the curingblowing behavior and physical properties of NR/SBR foam was investigated.
结果表明，将不同的CM并用改善了硫脲-硫黄硫化体系的硫化行为，出现了硫化平坦区。
The results showed that the vulcanization behavior of CM was improved by the blending of CMs in thiourea type accelerated-sulfur system, with which the flat part of vulcanization appeared.
简要论述了操作油、防老化体系、硫化体系、操作助剂和偶联剂等的选择对胶料滚动阻力的影响。
The influence of processing oil, antioxidant, curing system, processing aids and coupling agent on the rolling resistance of rubber compound is also briefly described.
结果表明，采用普通硫化体系、半有效硫化体系的效果明显优于有效硫化体系及无硫黄硫化体系。
The results showed that the effectiveness of conventional curing system or semi efficient curing system was much higher than that of efficient curing system or non sulfur curing system.
研究了双酚硫化体系的硫化剂双酚AF和促进剂BPP的变量对氟橡胶硫化特性和物理性能的影响。
This paper presents researches that AF and BPP's variables have impacts on F-rubber's sulfuration and physics properties.
这一优点是单独使用过氧化物，以及使用过氧化物硫磺与其它助交联剂的组合作为硫化体系所不具备的。
The advantages are not possessed by the curing systems that singly use peroxides and the combination of the peroxide sulphur and other auxiliary crosslinking agents.
探索硫化体系对EPDM加工行为、力学性能的效应，同时注重于硫化体系对硫化胶及制品喷霜的效应。
The effects of curing system on EPDM processing behaviour. its physical properties, and on vulcanizate and its products were explored. It was found that the compounding ZDC/T.
研究了共混比、硫化体系、增强剂、软化剂和硅烷偶联剂对IIR/CIIR共混胶动态力学性能的影响。
The effects of blend ratio, curing system, reinforcement agents, soften agents and silane coupling agents on dynamic mechanical properties of IIR/CIIR blends were researched.
讨论了低硫高促硫化体系EPDM制品的亮度和模具污染的问题，研究了微型汽车后轮制动缸皮碗的配方。
The problems of glittering of EPDM products with low sulfur and high accelerator vulcanization system and its mold pollution were discussed.
试验结果表明，通过调整生胶品种、补强体系和硫化体系等，可以改善胎面胶的耐磨性能，降低胶料成本。
The test results showed that the wear resistance of tire tread improved and the compound cost reduced by changing the rubber type, filler system and curing system.
试验结果表明，通过调整生胶品种、补强体系和硫化体系等，可以改善胎面胶的耐磨性能，降低胶料成本。
The test results showed that the wear resistance of tire tread improved and the compound cost reduced by changing the rubber type, filler system and curing system.