用中性盐雾腐蚀试验来评价复合材料的耐蚀性，并用XRD检测了腐蚀产物。
Finally, the corrosion resistance of samples is evaluated by neuter salt-spray tests and corrosion products are confirmed by XRD.
在盐雾试验或其它试验后沿着划线涂层边缘的腐蚀。
Corrosion under a scribe line or an area of damaged coating or edge, after salt spray testing or other testing.
化学性能测试：材料的盐雾试验、不锈钢腐蚀试验等。
Chemical property testing: salt spray test of materials, corrosion test of stainless steel.
涂层金属耐腐蚀性的电化学测定方法简便，快速，比盐雾试验和大气曝露等常规方法提供较多信息。
The electrochemical determination of corrosion resistance of coated metals is more easy and simple compared to the salt fog test and atmosphere exposure and may provide more information.
通过高温抗氧化、盐雾腐蚀和应力腐蚀试验研究了07X16H6沉淀硬化不锈钢在使用状态（回火态）时的耐蚀性能。
The corrosion resistance of 07X16H6 precipitation hardening stainless steel in tempered state was studied using high temperature oxidation, salt-spray test and stress corrosion test.
以45钢、A3钢、炮钢、20钢为金属试样，研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
介绍了盐雾试验箱的构造，工作原理和试验方法，并探讨了涂层在循环腐蚀试验中的诸多影响因素。
This article has described the structure, operation principle and test method of salt spray cabinet, and discussed various factors that influence the cycle corrosion test.
产品的镀层有规定的工艺要求，并经过一定时间盐雾试验，在规定的时限内无腐蚀。
The Chrome Coating has its industry standard, and tested by salt spray, without eroded at the stated hour.
中性盐雾、电化学测试等腐蚀性能试验结果表明，钛盐钝化溶液所获得的蓝色钝化膜，其耐腐蚀性能更优于铬酸盐钝化膜。
Corrosion resistance of the blue passivation film obtained in titanium salt solution was superior to that of the chromate passivation.
大功率二次风喷涂的锌铝伪合金耐腐蚀层在盐雾试验中能够达到16 000小时长效保护。
The Zn-Al pseudo-alloy anticorrosion layer of high-power twice breezes spraying in the salt fog test can be achieved a long-term effect protection about 16 000 hours.
所获得的黑色钝化膜外观均匀，镀层钝化后经中性盐雾试验(连续喷雾)出现红锈(基体腐蚀)的时间大于1000小时。
The black inactivating film is homogeneous, and the inactivated coating, test shows, has a no red rust period longer than 1000 hr in neutral salt fog.
所获得的黑色钝化膜外观均匀，镀层钝化后经中性盐雾试验(连续喷雾)出现红锈(基体腐蚀)的时间大于1000小时。
The black inactivating film is homogeneous, and the inactivated coating, test shows, has a no red rust period longer than 1000 hr in neutral salt fog.