薄膜电阻率随退火温度的变化行为与薄膜微观结构的变化以及界面扩散有关。
The annealing behavior of the resistivity is correlated with the microstructure and interfacial diffusion of the films.
用电阻应变片法测试了管棒材拉拔、矫直和退火过程中产品表面残余应力，研究了管棒材残余应力随工艺参数变化的规律。
The surface residual stress of tube and bar after drawing straightening and annealing, under different processing conditions, were measured by means of resistance strain gauge.
当退火工艺变化时，电阻系列热双金属的电阻率和温曲率等主要性能将产生变化。
The resistivity and flexivity of the resistance thermostat metal change while the anneal process change.
用途：台车式电阻炉系周期作业式电炉，可供大中型金属机件和材料的正火、淬火退火等热处理和加热之用。
Applications: the bogie hearth electric resistance furnace is a batch type furnace, it is used for normalizing, quenching, annealing and other heat treatments of large or medium metal parts.
随退火温度升高，合金丝电阻率下降，热电势升高。
As the annealing temperature rises, the resistivity of alloyed wire reduced and thermal potential raised.
井式电阻炉经技术改造后提高了钢丝的退火质量，降低了能耗。
Through doing some technical remakes on well resistance furnace the annealing quality of steel wire has been improved and the energy consumption has been cut down.
实验结果表明：退火后样品的薄膜电阻率显著减小，是未退火样品薄膜电阻率的3.17分之一；
The experimental results indicated that the film resistivity of the sample annealed was reduced significantly and only one 3.17 of the unannealed.
研究了高速钢轧材在台车式电阻炉中退火加热过程中，各因素对脱碳的影响。
The effects of various factors on decarburization of high speed tool steel annealed in bogie hearth electric furnace were investigated in this paper.
随着退火温度的升高，电阻率减小。
With increasing the annealing temperature, electrical resistivity decreases.
SOI衬底顶层硅呈现高阻状态，合适温度的退火可以明显降低SOI衬底顶层硅电阻率，也可部分减少外延高阻过渡层厚度。
The annealing at the proper temperature may decrease the resistivity of SOI substrate obviously and also improve the resistivity of epitaxial transitional layer partly.
随着退火温度的上升，薄膜表面质量下降，分形维和电阻率也随之降低。
The results indicate that the surface quality, FD and resistivity of the film increase with the sputtering time, but decrease with the Annealing temperature.
采用离子束溅射方法制备了正巨磁电阻多层膜，在制备过程中采用外加磁场和退火处理。
A series of giant positive magnetoresistance of magnetic multilayer structure were fabricated by ion-beam sputtering in high vacuum with applied magnetic field and treatment.
进行第二次退火以便将通过第一次退火的两次热循环形成的富金属硅化物相转化成处于其最低电阻相的金属硅化物(68)相。
A second anneal is performed to convert the metal rich silicide phase formed by the two thermal cycles of the first anneal into a metal silicide (68) phase that is in its lowest resistance phase.
同时发现退火处理对样品的电阻率有重要的影响。
Also it has been found that annealing processing affects the resistivity significantly.
溅射工艺制备出的铝背场接触电阻随退火温度升高呈下降趋势且溅射工艺的接触电阻比印刷工艺更小。
The back ohmic contact resistance of Al-BSF by DC magnetron sputtering is downtrend with the annealing temperature increasing, and less than that by the screen printing process.
薄膜室温电阻率随着退火温度的上升， 呈先上升、后下降趋势；
With the annealing temperatures increasing, the room temperature resistivity of the films rises at the beginning, then goes down.
实验结果表明：通过控制基体温度和退火条件(退火温度及退火时间等)可以改变膜电阻。
The result shows that: The resistance of films are changed with substrate temperature and annealing conditions (annealing temperature and annealing time).
实验结果表明：通过控制基体温度和退火条件(退火温度及退火时间等)可以改变膜电阻。
The result shows that: The resistance of films are changed with substrate temperature and annealing conditions (annealing temperature and annealing time).