扫描电镜(SEM)观察认为，贮氢合金在充放电过程中的不断粉化和氧化是贮氢电极失效的主要原因。
The SEM observation considered that the pulverization and oxidation of hydrogen storage alloys during charge discharge cycles was a important factor of the degradation of MH electrodes.