电弧炉炼钢是用来生产特殊钢和高合金钢的主要方法。
The electric arc furnace (EAF) steelmaking is the main method used to produce special steel and alloy steel.
根据测量结果建立了石钢32MV.A高阻抗电弧炉工作电抗模型。
The non-linear operation reactance model of the 32 MV·A high impedance electric arc furnace was established.
电弧炉用来生产特殊钢比用任何其他炉子都好，因为它不需要燃料。
The electric arc furnace is better for the production of special steels than any other types of furnace, since it needs no fuel.
这一系统可以接受、分配、发放和储存用电弧炉、钢包炉和钢排气操作来生产钢的焊剂和合金原料。
The systems can be designed to receive, dispense, deliver and store flux and alloy raw materials used in the production of steel at electric arc furnace, ladle furnace, and ladle degassing operations.
而对于电弧炉冶炼的高氮钢，宜采用铝和钛同时加入工艺。
With regard to high nitrogen 20CrMnB steels produced by EAF, simultaneous addition of Al and Ti is applicable.
该模型可动态地模拟电弧炉冶炼过程中的废钢量、炉温、渣量、钢液成分、炉渣组成和炉气成分的变化。
With this model the EAF Steel-making process can be simulated, including of scrap melting procedure, the changes of temperature, slag quantity and compositions of steel, slag and off-gas.
江苏苏钢集团电弧炉炼钢烟尘含锌15.4%，并主要分布在铁酸锌中。
The electric arc furnace dust in Jiangsu Sugang Group contains Zn content of 15.4% and is mainly embedded in zinc ferrite.
通过生产试验研究了电弧炉冶炼过程、L F精炼过程及连铸过程钢液氮的控制。
The experimental study on control of nitrogen in liquid steel during EAF melting, LF refining and continuous casting have been carried out.
与普碳钢或低合金钢厂电弧炉烟尘比较，不锈钢电弧炉烟尘含有更多的合金元素，但锌含量较低。
Comparison with EAF dust at carbon and low alloy steel works, the EAF dust at stainless steel works contains more alloy elements but zinc content is lower.
电弧炉炼钢可以分为以下4个阶段：装料，熔化，精炼和出钢。
The electric arc steelmaking process may be divided into the following four stages: charging, melting, refining and tapping.
提出了电弧炉炼钢比较优势分析框架，将电炉钢和转炉钢作为替代品进行比较，得出了电炉炼钢的优势及影响其应用的因素。
An analytical frame work is developed by treating the BOF steel as EAF steel's substitutes, Then the application potential and application potential are gotten using the framework.
分析了真空白耗电弧炉铜-不锈钢异种金属套管式电极杆焊接裂纹产生的机理。
The mechanism of welding crack generation in the copper - stainless steel tube electrode stem of Vacuum Consumable Arc Furnace has been analyzed.
超高功率电弧炉出钢口在使用过程中要经受钢液的冲刷、渣液的侵蚀、氧化和温度的剧烈变化。
The taphole of UHP-EAF should stand severe molten steel corrosion, slag erosion, oxidation and temperature change during operation.
目前在攀长钢，不合理的LF精炼工艺已经成为制约“电弧炉—LF炉—（VD/VOD炉）—连铸或模铸”高效炼钢的瓶颈。
Nowadays in Changcheng Steelworks, the unreasonable LF process has become the bottleneck for high speed steelmaking of "EAF-LF-(VD/VOD)-CC/ingot casting".
目前在攀长钢，不合理的LF精炼工艺已经成为制约“电弧炉—LF炉—（VD/VOD炉）—连铸或模铸”高效炼钢的瓶颈。
Nowadays in Changcheng Steelworks, the unreasonable LF process has become the bottleneck for high speed steelmaking of "EAF-LF-(VD/VOD)-CC/ingot casting".