本工作应用背散射电子衍射技术测得产生浮突的位移在不变线方向附近。
The displacement vector for surface relief was determined to be near the invariant line direction using electron back scattering diffraction method.
利用高能反射电子衍射技术（RHEED），研究了硅、锑化铟、碲镉汞样品逐次化学腐蚀后的切割表面损伤。
Surface damage caused by cutting on Si, InSb, HgCdTe has been studied by Reflection High Energy Electron Diffraction (RHEED) after step-etching the samples.
采用扫描电子显微技术（SEM）、透射电子显微技术（TEM）、背反射电子衍射技术（EBSD）等分析手段对AA2195铝锂合金过时效对析出相粒子组态、细晶组织的影响进行了研究。
The influence of over-aging treatment of AA2195 on the distribution of second phase particles was investigated by SEM, TEM, and electron back scatter diffraction(EBSD).
虽然阿西莫夫虚构的“正电子”大脑并不存在，但是正电子理论确确实实被应用于正电子衍射成像(PET)扫描技术上用来探索人类大脑。
And although Asimov's "positronic" brains do not exist, positrons are indeed used to probe human brains in positron-emission tomography (PET) scanning.
用两种会聚束电子衍射(CBED)技术研究了复合材料界面残余应变场。
The residual strain fields at composites interface were studied with two convergent beam electron diffraction (CBED) techniques.
利用背散射电子衍射取向成像技术，定量分析了具有初始织构的AZ31镁合金平面应变压缩时的孪生过程。
The twinning process in a magnesium AZ31 alloy with initial texture is quantitatively analyzed during plane-strain compression by means of orientation mapping based on EBSD technique.
利用背散射电子衍射取向成像技术定量分析了热模拟单向压缩条件下Q235碳素钢热变形时铁素体的织构形成规律。
The texture evolution of ferrite during warm compression of Q235 low carbon steel was determined quantitatively by means of orientation mapping based on the EBSD technique.
利用背散射电子衍射取向成像技术定量分析了热模拟单向压缩条件下Q235碳素钢热变形时铁素体的织构形成规律。
The textural features during ferrite refinement by deformation enhanced transformation were analyzed by means of orientation mapping based on the EBSD technique in a Q235 low carbon steel.
利用背散射电子衍射取向成像技术分析了在热模拟单向压缩条件下Q235碳素钢应变强化相变中铁素体晶粒的取向（差）变化特点。
The microstructure evolution of Q235 plain carbon steel in multi-pass hot deformation was investigated by means of hot compression simulation.
并利用背散射电子衍射(EBSD)技术分析了晶粒取向变化。
The grain orientation was determined by orientation mapping of EBSD technique.
并利用背散射电子衍射(EBSD)技术分析了晶粒取向变化。
The grain orientation was determined by orientation mapping of EBSD technique.