采用恒电压电解法研究了铝在硫酸中的阳极氧化过程。
The anodic oxidation process of aluminum in sulfuric acid was investigated using constant voltage electrolysis method.
传统铝的硬质阳极氧化需要较低的温度和较高的电压。
Traditional aluminum hard anode oxidation needs lower temperature and higher voltage.
另外，研究了阳极氧化电压对晶胞尺寸、孔径大小、孔密度和晶胞密度的影响。
Furthermore, the effect of anodizing voltage on cell sizes, pore diameter, pore density and cell density are studied.
采用正交实验研究了阳极氧化时温度、时间、电压对氧化铝膜厚度、孔径和孔有序度的影响。
The influences of temperature, time and voltage on the thickness of oxidation film, aperture and order degree during anodic oxidation were studied by orthogonal test.
介绍了电参数如频率、占空比、电流密度、终电压等的概念，推导了占空比与电流密度的关系，并综述了电参数对阳极氧化膜性能影响的研究进展。
Concepts of some electric parameters such as frequency, duty cycle, current density and final voltage were introduced and the relation between duty cycle and current density was deduced.
过高的阳极氧化电压和HF浓度导致钛表面局部区域腐蚀，部分生成的纳米管产生塌陷。
The high voltage and concentration of HF solution lead to corrosion of the surfaces of TiO2 nanotube arrays.
过高的阳极氧化电压和HF浓度导致钛表面局部区域腐蚀，部分生成的纳米管产生塌陷。
The high voltage and concentration of HF solution lead to corrosion of the surfaces of TiO2 nanotube arrays.