将聚苯乙烯溶解在甲基丙烯酸甲酯单体或其与苯乙烯的混合液中进行原位聚合，制备高散射有机玻璃导光材料。
High scattering optical transmission PMMA was prepared by the in situ copolymerization of methyl methacrylate and styrene with polystyrene.
这些化合物能均聚反应，亦易与苯乙烯、甲基丙烯酸甲酯及丙烯腈等乙烯类单体共聚合，得有色的高聚物。
These colored compounds can be homopolymerized and copolymerized with most vinyl monomers such as styrene, methyl methacrylate and acrylonitrile, to give the corresponding colored polymers.
以最常见的两种单体甲基丙烯酸甲酯和苯乙烯为例。
Take the most widely used monomers, styrene and methyl methacrylate as an example.
配方：溶剂：醋酸，单体中甲基丙烯酸甲酯体积分数为10%到30%。
The recipe: acetic acid as solvent, MMA contents from 10 vol % to 30 vol %.
以甲基丙烯酸甲酯为硬单体，丙烯酸丁酯为软单体，丙烯酸为功能单体，环氧树脂为改性剂制备了密封胶用环氧改性丙烯酸树脂。
The epoxy modified acrylate resin for sealant is prepared with methyl acrylate as hard monomer, butyl acrylate as soft monomers, acrylate acid as functional monomers and epoxy resin as modifier.
研究了聚甲基丙烯酸甲酯大单体与丙烯酸丁酯在苯中的共聚。
The poly macromer was copolymerized with butyl acrylate in benzene to form the graft copolymer.
本论文采用乳液聚合的方法合成了聚醋酸乙烯树脂，并通过加入硬单体—甲基丙烯酸甲酯对其进行改性。
The method of emulsion polymerization was used to synthesize polyvinyl acetate resin by adding hard monomer_methyl methacrylate to modify it.
接枝物极性的增加的趋势依次按接枝单体马来酸酐（MAH）、甲基丙烯酸甲酯（MMA）、甲基丙烯酸缩水甘油酯（GMA）递增。
The increasing order of the polarity of the grafted PP was as this sequence: MAH, MMA and GMA, which showed the ef.
甲基丙烯酸甲酯（MMA）是合成有机玻璃及MBS树脂的单体。
Methyl methacrylate (MMA) is a monomer that is used to polymerize the organic glass and the MBS resin.
以丙烯酸、 丙烯酸丁酯和甲基丙烯酸甲酯为单体，采用自由基聚合法制备了聚丙烯酸卷材涂料前驱成膜物，获得了适宜的制备工艺条件。
Phragmoplast of coil coating has been prepared by free radical polymerization and by using acrylic acid, methyl methacrylate, butyl acrylate as the raw materials.
介绍了以丙烯酸、丙烯酸十二酯、甲基丙烯酸甲酯和丙烯酸丁酯为单体，采用反应型乳化剂，经过乳液聚合，制得了一种水性涂料用缔合型增稠剂。
A kind of associative thickener for waterborne coating is prepared by emulsion polymerization of acrylic, lauryl acrylate, methyl methacylate and butyl acrylate as monomers and reactive emulsifier.
以甲基丙烯酸甲酯为主的硬质非弹性无规共聚物由甲基丙烯酸甲酯和能与其共聚的单体组成。
The hard non-elastic atactic copolymer with methyl methacrylate as main component consists of methyl methacrylate and monomer capable of copolymerizing with it.
以甲基丙烯酸甲酯为主的硬质非弹性无规共聚物由甲基丙烯酸甲酯和能与其共聚的单体组成。
The hard non-elastic atactic copolymer with methyl methacrylate as main component consists of methyl methacrylate and monomer capable of copolymerizing with it.