本工作定量测定了2-乙烯基吡啶-甲基丙烯酸甲酯-铑络合物的烯烃催化加氢性能与共聚物配体序列结构的关系。
The quantitative relationships between the catalytic ability of Rh-complex of 2-vinyl pyridine-methyl methacrylate copolymer and the sequence structures of the copolymer ligands have been determined.
在乙醚溶液制得的聚苯乙烯次甲基锂与甲基丙烯酸甲酯反应不能分离出聚甲基丙烯酸甲酯及它的接枝共聚物。
Neither polymethylmethacrylate nor polymethylmethacrylate-grafted copolymer could be isolated by the reaction of polystyrene methylene lithium prepared in ether solution with methyl methacrylate.
以醋酸乙烯酯和丙烯酸丁酯为主要原料，引入自交联型单体羟甲基丙烯酸胺合成了纸张——铝箔复合膜粘合剂。
The self - cross linking adhesive for paper - Al foil composite can be abtained by using vinyl acetate and acrylate as raw materials and hydroxy methyl acrylamide as self - cross linking monomer.
这些化合物能均聚反应，亦易与苯乙烯、甲基丙烯酸甲酯及丙烯腈等乙烯类单体共聚合，得有色的高聚物。
These colored compounds can be homopolymerized and copolymerized with most vinyl monomers such as styrene, methyl methacrylate and acrylonitrile, to give the corresponding colored polymers.
以最常见的两种单体甲基丙烯酸甲酯和苯乙烯为例。
Take the most widely used monomers, styrene and methyl methacrylate as an example.
以二乙烯基苯为交联剂，由甲基丙烯酸甲酯、苯乙烯、甲基丙烯酸模型浇铸共聚，制得了一种交联型改性有机玻璃。
A kind of crosslinking modified organic glass was prepared by mold copolymerization of methyl methacrylate, styrene, methacrylic acid with divinylbenzene as crosslinking agent.
合成了1 ，2 -二哌啶乙烷，并将其应用于苯乙烯和甲基丙烯酸甲酯的原子转移自由基本体聚合。
The new ligand 1,2-dipiperidinoethane (DPE) was designed and synthesized, and applied to atom transfer radical polymerization of styrene and methyl methacrylate monomers.
本论文采用乳液聚合的方法合成了聚醋酸乙烯树脂，并通过加入硬单体—甲基丙烯酸甲酯对其进行改性。
The method of emulsion polymerization was used to synthesize polyvinyl acetate resin by adding hard monomer_methyl methacrylate to modify it.
热固型丙烯酸涂料是由丙烯酸和甲乙基丙烯酸酯，丙烯酸和甲基丙烯酸，或苯乙烯反应而成。
Thermoset acrylic coating are based on resins prepared from acrylic and methacrylic esters, acrylic and methacrylic acids, and / or styrene.
三元树脂由乙烯基磺酸酯、甲基丙烯酸甲酯（MMA）与甲基丙烯酸（MAA）按不同的配比共聚而成。
The polymer was prepared by copolymerizing vinyl sulfonate, methyl methacrylate(MMA) and methacrylic acid(MAA) in different proportions.
实验研究工作以四针状氧化锌晶须为填料，以聚乙烯醇和聚甲基丙烯酸甲酯为基体，以水和甲苯为溶剂，制备出了性能良好的导电膜。
In the study on manufacture of the composites, tetrapod-like ZnO whiskers, PAV and PMMA, water and toluene, are employed as conductive fillers, matrix materials and solvents respectively.
以甲基丙烯酸、苯乙烯、丙烯酸羟乙酯和丙烯酸- 2 -乙基己酯为主要原料，通过溶液共聚法合成了用于丙烯酸酯水性涂料的高分子表面活性剂。
A new polymeric surfactant using for acrylic acid waterborne coatings was prepared from the methyl acrylic acid, styrene, hydroxyethyl acrylate and 2-ethylhexyl acrylate.
将聚苯乙烯溶解在甲基丙烯酸甲酯单体或其与苯乙烯的混合液中进行原位聚合，制备高散射有机玻璃导光材料。
High scattering optical transmission PMMA was prepared by the in situ copolymerization of methyl methacrylate and styrene with polystyrene.
文章研究了苯乙烯-甲基丙烯酸甲酯树脂的制备，并研究了该树脂对铜离子的吸附性能。
The paper changed a various of experimental conditions, emphasized to study the synthesis of the resin of styrene-methyl methacrylate, and then studied its adsorption performance to the cupric ion.
介绍了医用塑料的分类、特点，阐述了聚氯乙烯、液晶聚合物、聚甲基丙烯酸甲酯等在医疗器械、医疗用品、人工脏器等方面的应用；
The classification and characteristics of the medical plastics are introduced. The application of PVC, liquid crystal polymer, PMMA, etc. in the medical and hygienical fields is explained.
本工作研究了由蓖麻油型聚氨酯及苯乙烯、甲基丙烯酸甲酯、丙烯腈的均聚物或共聚物组成的互穿网络物在室温条件下的合成规律。
The Conditions for formation of IPN from castor oil polyurethane and homopolymer or copolymer of styrene, methylmethacrylate and acrylonitrile at room temperature were Studied.
采用悬浮聚合方法合成了苯乙烯-甲基丙烯酸缩水甘油酯（GMA）共聚物（SG） ，讨论了各种实验条件对聚合反应的影响。
Styrene-glycidyl methacrylate copolymer (GMA) was synthesized by suspension polymerization, and the effect of various experimental factors on the polymerization were also studied.
结果发现，甲基丙烯酸甲酯接枝的炭黑在高密度聚乙烯中能表现出较好的PTC效应。
The effects of various grafting CB for conductive particles in the PTC composites were investigated. It showed that PTC properties of MMA g CB/HDPE composites were improved.
本文研究了苯乙烯、甲基丙烯酸甲酯、二氧化硫三元共聚合反应。
The ternary copolymerization of styrene, methylmethacrylate and sulfur dioxide was studied in this paper.
本文对以甲基丙烯酸甲酯预聚物（Pr-MMA）为光散射体，以聚苯乙烯（PS）为基体的有机光散射材料的制备进行了研究。
The thesis makes researches into taking the pre-polymer of methyl methacrylate (Pr-MMA) as light scattering substance, and polystyrene (PS) as matrix to make organic light scattering materials.
本发明公开了一种聚乙烯接枝甲基丙烯酸缩水甘油酯的方法。
The invention discloses a method for polyethylene to graft glycidyl methacrylate.
用自行合成的带有可聚合活性基团的硫杂杯芳烃衍生物，分别与苯乙烯和甲基丙烯酸甲酯聚合，得到不同组成配比的两类七种新共聚物。
In this paper, a thiacalixarene derivative with active double-bond was synthesized, and which was as a monomer copolymerized with other monomers by solution polymerization, yield 7 new copolymers.
用自行合成的带有可聚合活性基团的硫杂杯芳烃衍生物，分别与苯乙烯和甲基丙烯酸甲酯聚合，得到不同组成配比的两类七种新共聚物。
In this paper, a thiacalixarene derivative with active double-bond was synthesized, and which was as a monomer copolymerized with other monomers by solution polymerization, yield 7 new copolymers.