料浆愈稳定,生坯密度愈高,微观结构愈均匀,但吸浆速度减慢。
The higher the suspension stability, the higher the green density, and the more homogenous the microstructure, but the smaller the permeation rate.
测定了它们的冷压生坯密度、模拟生坯强度以及高频钎焊的结合力矩;
Green-pressing density, simulated green-pressing strength and bonding momental of high frequency brazing were assayed.
研究电解铜粉高速压制成形工艺,探讨冲击能量、压制次数对生坯密度、最大冲击力和脱模力的影响。
The effects of impact energy and impact times on the green density, the maximal impact force and the withdraw force of specimen were investigated.
研究电解铜粉高速压制成形工艺,探讨冲击能量、压制次数对生坯密度、最大冲击力和脱模力的影响。
The effects of impact energy and compaction methods on the green density, the maximal impact force, the withdraw force and the radial springback were discussed.
随成型压力的增加,当保压一定时间、添加一定量助烧剂时,生坯密度随之增加,饱和磁化强度也相应提高。
With the increase of molding pressure, holding pressure for certain time and adding a certain amount of boric acid doping, the compact density and saturation magnetization correspondingly increase.
为保证绝缘子获得较高致密度而不变形,应尽量提高生坯密度,同时排蜡温度应低于该种玻璃的转变温度上限。
To insure more densification but deformation of glass beads, the green density should be increased, and the burnout temperature of binder should be below the toplimit of transformation temperature.
试验结果表明:温压工艺能够较大幅度地提高316L不锈钢粉末的生坯密度和生坯强度,也能提高其烧结后的密度和抗拉强度。
Results show that warm compaction can improve the green density and strength of 316L powder greatly and improve its sintered density and tensile strength as well.
温压工艺可达到比传统铁粉压块更高的密度与生坯强度。
Warm compaction process yields higher density and improved green strength over conventionally processed iron powder compacts.
对于一定粒度的碳化硅粉而言,加入到生坯中碳粉粒度应小于一定尺寸,否则,陶瓷的断裂强度和密度将随碳粉粒度的增大而降低。
For the green body containing a certain size of SiC powders, the carbon particle should be less than a certain size, or else, the density and fracture strength of RBSC decrease wit...
在较低的固相含量和较高的离心加速度下,浆料的分离现象明显,生坯中出现密度梯度。
The mass segregation phenomenon became more obvious at lower solid content and higher acceleration and there were density gradient in green compacts.
在较低的固相含量和较高的离心加速度下,浆料的分离现象明显,生坯中出现密度梯度。
The mass segregation phenomenon became more obvious at lower solid content and higher acceleration and there were density gradient in green compacts.