以含环氧基聚二甲基硅氧烷为基胶,以胺类化合物为固化交联剂进行了新型加成型硫化硅橡胶的研究。
By using polydimethylsiloxane containing epoxy groups as base gum, the compounds containing amino groups as crosslinking reagent, a new addition type curable silicone rubber were prepared.
再与低含氢硅油进行硅氢加成反应,合成出环氧聚醚改性聚甲基硅氧烷;
It was then reacted with low hydrogen containing silicone oil via hydrosilylation to produce epoxy-containing polyether silicone.
利用微波等离子体化学气相沉积方法,以H 2、CH4和八甲基环四硅氧烷(D4)为原料,在硬质合金基体上沉积了金刚石涂层。
Diamond coatings were deposited on cemented carbide substrates with H2, CH4 and D4 as precursors by using microwave plasma chemical vapor deposition technique.
聚甲基苯基硅氧烷(PMPS)接枝改性E-20环氧树脂。
E-20 epoxy resin was grafted by polymethylphenyl silicone(PMPS).
以苯基环体、二甲基环硅氧烷为原料,在催化剂存在下,经开环共聚、降解、脱除低沸物,制得低苯基含量的二苯基硅橡胶。
Dimethyldiphenyl RTV silicone rubber with low phenyl contents was synthesized by ring opening copolymerization of phenyl cyclic siloxane with DMC.
采用七甲基乙烯基环四硅氧烷和丙烯酸酯类单体,用乳液聚合的方法同时对明胶改性制作皮革涂饰剂。
In the research, organic silicon and acrylic esters were used to modify the gelatin as leather finishing coatings.
由1,3,5-三(甲基三氟丙基)环三硅氧烷的阴离子本体开环缩聚合成了氟硅生胶,并对生胶进行过氧化物交联。
Poly(methyl(trifluoropropyl) siloxane)(PMTFPS) was prepared by bulk ring-opening polymerization of 1,3,5-trimethyl-trifluoropropyl cyclotrisiloxane, and crosslinked by peroxide compound.
采用八甲基环四硅氧烷(D4)对聚苯胺(PANI)进行表面修饰。
The surface of PANI was modified by using octamethylcyclotetrasiloxane (D4).
采用八甲基环四硅氧烷(D4)对聚苯胺(PANI)进行表面修饰。
The surface of PANI was modified by using octamethylcyclotetrasiloxane (D4).