本文用微波法煅烧高岭土并合成4a沸石。
The calcination of Kaolinite and synthesis of 4a Zeolite with microwave method have been investigated.
介绍了该煅烧高岭土的生产工序及其在乳胶漆的应用。
The production process and its application in latex paint of this calcinated kaolin clay were described.
研究了超细煤系煅烧高岭土颗粒表面包覆二氧化钛膜的工艺。
The technology of coating TiO 2 film on the surface of ultra fine calcined coal kaolin particle was studied.
研究表明: 掺入10% 煅烧高岭土的水泥的性能得到大幅度地提高;
The result showed that the performance of cement improved greatly with 10% of calcined argilla.
提出该资源应以开发煅烧高岭土为主,为开发鄂西山区资源指出了方向与途径。
Indicated developing the source should be mainly on calcined kaolin. Pointed out the direction and ways of developing the source in west of Hubei.
提出该资源应以开发煅烧高岭土为主,为开发鄂西山区资源指出了方向与途径。
Pointed out the direction and ways of developing the source in west of Hubei.
公司投产以来,所生产的超细、超白煅烧高岭土的各项指标均达到或超过行业标准。
Since the company's production, the production of ultra-fine, ultra-white calcined kaolin of the indicators have reached or exceeded industry standards.
煅烧高岭土掺入水泥中,增加了水泥石的化学收缩,对水泥石的自收缩的影响并不明显。
The addition of calcined kaolin to cement increased the chemical shrinkage of cement stone, but it had no distinct impact on the self-shrinkage of cement stone.
内蒙古华生高岭土有限责任公司是一家由华立集团控股,专业生产及研发高品质煅烧高岭土的公司。
Inner Mongolia Huasheng Kaolin Co. , Ltd. is held by Holley Group. It is specialized in manufacturing and R&D of calcined kaolin.
机械力化学效应使煤系煅烧高岭土产生的高活性表面和化学活性点为其进一步深加工提供了有效途径。
The high actived surface or many chemical actived spots of ultrafinecalcinated coal kaolin are casier interact to surface modifiers, h…
另外,由于煅烧高岭土有很好的松散特性,使得深层更迅速胶凝,改进了涂料的固着性能,有效降低造纸费用。
In addition, As well calcined kaolin loose, which makes deep gel more quickly, improving the paint with solid performance reduce paper costs.
研究了煅烧过程中白度的变化规律,成功地找到了提高该地区煅烧高岭土白度较有效的添加剂。为进一步扩大实验和开发利用该区高岭土资源提供了依据。
Its whiteness change law in the roasting process was studied and different additive for improving the roasted kaolin whiteness of this mine district were successfully found.
高岭土及类似土,不论是否煅烧。
考察了不同煅烧温度下前驱体粉末的活性、不同高岭土添加量以及不同淀粉添加量对成型脱硫剂有效硫容的影响。
The activity of precursor powder at different calcination temperatures and the influence of kaolin and starch additional on the effective sulfur capacity of shaped desulfurizer were investigated.
利用析因实验方法,对低温煅烧的高岭土因受热的差异而对其活性所造成的影响进行了试验研究。
By the way of factorial experiment, authors studied the activity of kaolinite calcined under the condition of low temperature.
煅烧处理过的高岭土经水热反应后得到纳米级莫来石复合晶体,TEM观测到其晶粒发育良好。
The composite nanocrystalline of mullite was prepared via hydrothermal reaction of calcined kaoline. It was observed that growth of the nanocrystalline grain was good in TEM.
以湖北松宜煤系高岭土为原料,研究了煤系高岭土煅烧过程中煅烧温度、保温时间、升温速度、添加剂等因素对煅烧产品白度的影响。
Some experimental research was conducted on the effect of the calcining temperature, remaining time, temperature system of calcinations and additives on the whiteness of calcined kaolin.
本文以煤系高岭土为研究对象,研究了不同的煅烧条件对产品物化性能的影响。
Effect of different calcination conditions on physical and chemicalproperties of calcined coal kaolin has been investigated in this dissertation.
实验结果表明,采用煅烧二次酸浸工艺能按照上述要求有效地调整该高岭土的成分。
Laboratory test results show that the use of a calcining and double step hydrochloride acid leaching technique can satisfyingly do it.
以吉林白山地区石炭、二叠煤系高岭土(或高岭石)为试样,进行了矿物成分、含量分析和研磨、 煅烧、添加不同漂白剂加工工艺实验。
The chemical constitution and mineral composition were analysed with a hard kaolin(kaolinite) of the Carboniferous-Permian coal measures strata, in Baishan region of Jilin province as the sample.
探讨了开滦唐山矿的煤系高岭土增白工艺,对酸浸脱杂的温度、酸质量分数及煅烧工艺制度进行了深入研究。
The brightening technology of kaolin co existed in coal was studied. The studied contents included temperature of removing impurities with acid, the concentration of acid and calcination technology.
探讨了开滦唐山矿的煤系高岭土增白工艺,对酸浸脱杂的温度、酸质量分数及煅烧工艺制度进行了深入研究。
The brightening technology of kaolin co existed in coal was studied. The studied contents included temperature of removing impurities with acid, the concentration of acid and calcination technology.