研究了纯镍铸铁焊条冷焊时，稀土金属镧、铈、镨、钇及钕对焊缝热裂纹敏感性的影响规律，并分析了铈对焊接接头力学性能和加工性能的影响。
The influence of Lanthanum, Cerium, Yttrium, Praseodymium and Neodymium on weld hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron was studied.
WGJ510C2钢在自动埋弧焊焊评试验中所产生的裂纹均在焊缝金属中，与母材没有明显的相关性。
The cracks produced in the automatic SAW welding test are existed in the weld, and has nothing obviously with WGJ510C2 steel.
疲劳裂纹扩展速率和CTOD测试型不锈钢304研究和焊缝金属的温度范围-162度到另一个房间 温度。
The fatigue crack growth rate and CTOD tests on type 304 stainless steel and weld metal were studied over the temperature range -162 degree C to room temperature.
前轮对处于脆性温度区间的焊缝金属施加一个横向挤压塑性应变，减小甚至抵消致裂的拉伸应变，防止了焊接热裂纹的产生。
The front impact roller causes transverse plastic compression strain in the weld which is in the brittle temperature range, which counteracts the tensile strain which leads to hot cracking.
X65管线钢在焊接过程中，内侧焊缝金属出现横向和纵向沿熔合线方向的裂纹，横向裂纹贯穿焊缝金属横截面。
The longitudinal cracks along bond line and the transverse cracks which cut across the weld metal cross section inside weld metal were formed, while X65 pipe line steel was welding.
塔吊的紧固金属结构的联接螺栓和销轴，结构件不得有变形，焊缝不得有裂纹。
The bolt fastening metal structure of tower crane and pin structure without deformation, no weld crack.
结果表明，焊缝金属中存在的非金属夹杂物，在低应力作用下形成微裂纹成为裂源，加之焊缝组织中存在大量的MA结构群，从而发生焊缝金属在室温下的解理断裂。
The results showed that nonmetallic inclusions in weld seam served as crack initiation site under external bend load, and large amount of m a structure resulted in cleavage fracture of weld seam.
结果表明：随着焊缝中含镍量的增加，焊缝金属的凝固裂纹敏感性增大。
It was found that the solidification cracking susceptibility of weld metal increases remarkably as nickel content increases.
增加焊缝中的共晶数量并改善其分布形态，从而有助于降低焊缝金属的热裂纹敏感性。
The improvement of microstructure leads to a considerable reduction of the susceptibility of hot cracking of weld metal as indicated by the transverse-varestraint test.
文章分析了高强度X80钢管道的热影响区的软化、焊缝金属与母材的匹配及产生焊接裂纹的可能性，介绍了管道环缝焊接工艺，还列举了国外X80钢管道的焊接工程实例。
This paper analyzes the welding performances of the pipeline steel X80 including softening of heat affected zone, its matching with base material and the possibility of welding cracking. It also de…
文章分析了高强度X80钢管道的热影响区的软化、焊缝金属与母材的匹配及产生焊接裂纹的可能性，介绍了管道环缝焊接工艺，还列举了国外X80钢管道的焊接工程实例。
This paper analyzes the welding performances of the pipeline steel X80 including softening of heat affected zone, its matching with base material and the possibility of welding cracking. It also de…