在热裂试验的基础上,得到了铸件热裂纹倾向的临界值,进而实现了摇枕、侧架的热裂纹预测。
The critical value of hot crack has been obtained according to the experiments on test casting, and it had been used on predicting the hot crack of bolster and side bearer.
应用变形速率连续可变式热裂纹试验方法(VDR法)研究了碳、钼和稀土元素对奥氏体不锈钢焊缝热裂敏感性的影响。
The effect of carbon, molybdenum and rare earths on hot cracking susceptibility of austenitic stainless steel welds was studied with continuously variable deformation rate cracking test (VDR) method.
通过冷裂敏感性试验、焊接热影响区最高硬度试验及可调拘束试验,对新型铁路车辆用TCS耐蚀钢的焊接性进行了深入系统分析。
The weldability of TCS corrosion resistant stainless steel for railway wagon was investigated by cold cracking sensitivity test, HAZ maximum hardness test and varestraint test.
通过正交试验法获得了降低合金热裂倾向性的最佳工艺参数。
The reasons of effect factors on the hot cracking tendency are analyzed by orthogonal experimental method and the best technology parameters of decreasing hot cracking tendency are obtained.
采用理论计算、热影响区最高硬度试验和小铁研试验方法研究了超低碳含铜时效钢的抗裂性。
Cracking resistance of ultra-low cabon Cu-bearing age-hardening steels was studied in this paper by computing, maximum hardness in weld heat-affected zone test and Y-groove cracking test.
采用理论计算、热影响区最高硬度试验和小铁研试验方法研究了超低碳含铜时效钢的抗裂性。
Cracking resistance of ultra-low cabon Cu-bearing age-hardening steels was studied in this paper by computing, maximum hardness in weld heat-affected zone test and Y-groove cracking test.