同时,铝浆厚膜烧结层又作为背面电极。
Simultaneously, the SP aluminum thick film layer is the rear electrode.
烘炉是为了获得烧结层的过程,烧结层的好坏直接影响到了炉子的使用寿命,炉腔筑好后,应立即进行烘炉;
The oven is in order to obtain sintered layer, sintering layer directly affects the service life of the furnace, the furnace chamber was built, immediately before the baking oven;
玻璃表面有一层白色烧结的涂层并有一定的透明度。
The glass is coated with a solid white fritted finish with some degree of transparency.
采用扫描电子显微镜(SEM)对表面多孔管进行检测,结果显示用新工艺烧结的表面多孔层质量好、结合强度高。
After inspected by SEM, the results indicated that the porous surface tubes sintered by the new process had high quality and strong joint strength.
但低聚磷酸铵具有较低的熔点和烧结点,用来灭火时能迅速分解形成膜层覆盖于燃烧物表面使火焰熄灭。
But it has low melting point and sintering point, when it is used to extinguish a fire, it can rapidly decompose to form a layer of film, which can cover the surface of comburent and make the fire.
雅骏发明了电子束选择性烧结避免使用激光熔化粉末成层。
Arcam invented EBeam selective sintering to avoid using lasers to fuse powder into layers.
这是因为制粒后的烧结混合料里的较大焦粉颗粒燃烧效率更高,制粒效果更好,因而原始料层透气性和烧结透气性更好。
This was due to more efficient combustion of larger coke particles in a granulated mix and also to better granulation and therefore higher green feed permeability and sintering permeability.
通过扫描电镜分析,研究了厚膜铂电阻浆料在烘干、烧结过程中微观结构的变化,讨论了烧结过程中对膜层致密度的影响因素。
Changes of microstructure of the thick film platinum resistance paste during drying and sintering were studied by SEM. The main factors influencing tightness of the sintered membrane were discussed.
低碳厚料层烧结是一项重要的烧结技术,具有改善烧结矿质量、提高烧结矿强度、降低燃料消耗等优点。
Low carbon and thich sinter bed sintering is an important sintering technology, featuring the advantages of high quality, high strength and less fuel consumption.
通过料层温度测试、分析和对比,发现其固结方式类似于传统烧结法。
It was found through measurement, analysis and contrast of the heating patterns in the beds that the agglomerating mechanism of PSP is similar to that of conventional sintering process.
低碳厚料层烧结是一项重要的烧结技术,具有改善烧结矿质量、高烧结矿强度、低燃料消耗等优点。
Low carbon and thich sinter bed sintering is an important sintering technology, featuring the advantages of high quality, high strength and less fuel consumption.
乌石山矿可以改善烧结过层的透气性,提高垂直烧结速度并降低烧结矿的生产成本。
Wushishan iron ores can improve the sintering bed permeability and increase vertical sintering velocity, and decrease production cost of sinter.
实验结果表明,烧结温度对相层数量起主要作用,并和保温时间一起影响扩散溶解层厚度。
The results indicate that sintering temperature plays a prime role in the development of the number of phase layers and affects the thickness of diffusion solution layer by the thermal time.
厚料层烧结是一项很重要的烧结技术,具有改善烧结矿质量,降低燃料消耗等优点。
As a important sintering process, the deep-bed sintering play the roles of improving sinter quality and decreasing fuel consumption.
介绍过湿层形成机理,分析过湿层对烧结工艺过程的影响。
This paper introduces formation mechanism of overdamp layer and analyzes the effect on sintering process.
用中性玻璃与A-W生物活性玻璃陶瓷的混合陶瓷粉涂覆在TC4基体上,经预烧形成过渡层,然后再涂覆A-W陶瓷,经烧结来制备复合试样。
Coated by the mixed powders of neutro-glass and A-W bioactive glass ceramics on TC4 matrix and presintered to form a transition layer, the samples then were coated with A-W powders and sintered again.
介绍过湿层形成机理,分析过湿层对烧结工艺过程的影响。结合实际探讨减弱过湿层作用的具体措施。
This paper introduces formation mechanism of overdamp layer and analyzes the effect on sintering process. Some measures are discussed to weaken the layer of overdamp.
详细介绍了缩小主料斗喉口改善烧结料层透气度的原因,对ISP工艺烧结生产具有一定的指导意义。
The paper introduces the cause of reducing primary feeding hopper throat inlet to improve the ventilation of sintering mixture, which has certain significance to ISP process sintering production.
通过不同燃料偏析程度的烧结杯试验,说明酒钢酸性球团烧结工艺在上中下三层的合理燃料偏析程度是0.4%。
Based on pot tests with different carbon profile in sinter-bed, it is found that suitable degree of carbon segregation in three-layer is 0.4%.
随着烧结温度的升高,元素扩散加剧,过渡层的厚度越厚,材料的层间界面结合强度升高,石墨层与BN层结合的越好。
With increasing sintering temperature, the joint of graphite and BN was increased and also there was transition layer in the interfaces relative to HP.
介绍韶关冶炼厂烧结机烧结料层透气性的情况以及改造途径。
This paper describes the permeability of the sinter layers and proposes methods of improving it at Shaoguan Smelter.
该产品是以优质低碳钢板为基体,中间烧结一层多孔青铜层,表面轧制一层POM混合物。
The product is made of high quality low-carbon steel with sintering porous bronze as its interlayer, with the compound of POM as its surface.
该产品是以不锈钢为基体,中间烧结多孔青铜层,在表面轧制以PTFE为主的混合物,可在中酸、强酸中使用。
The product is based on stainless steel plate with sintering porous bronze layer and rolled PTFE compound 0n the surface. It can be used in strong acid and alkaline.
介绍了超声波式烧结环冷机料层厚度测量仪的系统构成和工作原理。
In This paper, the system composition and working principle of the material thickness measuring meter of ultrasonic sinter-circle-cooling machines are introduced.
松软的粉末在高温下烧结,陶土粒子即溶结成一层瓷釉。
The soft powder fired at high temperature until the ceramic particles melt and coalesce to form a glaze.
该产品以优质低碳钢为基体,中间烧结球形青铜层,表面轧制聚四氟乙烯和铅的混合物。
SF-1 carbon steel self-lubricating bearings used high quality low-carbon steel plate as base, sintered porous bronze as its interlayer and the Compound of PTFE and Lead as its surface.
本文分析了固体燃料在烧结料层中燃烧的热力学和动力学特征,着重从热力学和动力学角度讨论了降低包钢烧结矿固体燃耗的技术措施。
The energetic and dynamics property of solid fuel was analyzed and technical measures were put forward to reduce the energy consumption from the energetic and dynamics theory.
烧结坚持用好生石灰,推行厚料层 烧结,实施多项技术攻关,固体燃耗大幅度下降;
The solid fuel consumption of sinter has been decreased greatly through insisting on using high-quality calces, practising high feed sintering, actualizing many techniques in solving key problems.
烧结坚持用好生石灰,推行厚料层 烧结,实施多项技术攻关,固体燃耗大幅度下降;
The solid fuel consumption of sinter has been decreased greatly through insisting on using high-quality calces, practising high feed sintering, actualizing many techniques in solving key problems.