特点：熔炼速度快、高效节能、烧损率低，溶液纯净。
Features: Fast speed of melting, saving energy, less burnt loss, pure molten liquid.
讨论了不同结合剂与不同性质沥青相配合时修补料的烧结强度指数及烧损率的变化。
The changes of the sintering strength index and sintering loss rate of the mixes with different binders and pitches were discussed.
试验结果表明：在所有的焙烧实验条件下，烧损率的变化并不明显，在30 %左右；
The trial results are given as follows: under the experimental roasting conditions, it is not obvious to the change of weight-loss rate, and is about 30%;
T8涂层中由于碳元素被大量烧损，导致涂层氧化严重，孔隙率高，这是造成涂层硬度和强度不高及耐磨性较差的主要原因。
The burning loss of carbon, which causes heavy oxidation and high porosity, is the main reason for lower hardness, strength and worse wear resistance of T8 coating.
本发明可将合金粉末成团，当进入炼钢炉时，使其烧损小，收得率高，并且有减少环境污染的特点。
Saidresultant alloy briquette used for smelting steel features less ablation, high yield and decreasing environmental pollution.
针对热轧带钢加热炉能耗高、加热质量差、氧化烧损大、故障率高等问题进行技术改造，达到节能降耗的目的。
The reheating furnace in hot strip mill had high energy consumption, low heating quality, high metal loss and high failure rate.
针对热轧带钢加热炉能耗高、加热质量差、氧化烧损大、故障率高等问题进行技术改造，达到节能降耗的目的。
The reheating furnace in hot strip mill had high energy consumption, low heating quality, high metal loss and high failure rate.