产生裂纹漏钢的原因是多方面的。
铸坯裂纹漏钢在连铸生产过程中经常发生。
The billet crack breakout would take place often in the process of continuous casting.
粘结漏钢往往与所使用的结晶器保护渣性能有关。
Molten steel leakage by binding is often related to the properties of mould powder.
漏钢预报系统属于高效连铸生产的关键工艺和装备。
Breakout prediction system is a key technical equipment of high efficient continuous casting technique.
阐述了粘结漏钢的形成机理和漏钢预报系统的基本原理。
Formation mechanism of sticking breakout and basic principle of molten steel leakage prediction system are explained.
通过对邯钢CSP连铸机的漏钢分析，提出了预防措施。
The steel leakage of CSP caster is analyzed, some precaution proposed.
模拟得到生产良好复合轧辊、漏钢等不同的生产工艺条件。
Using the simulation can get the technique of good roll cladding, bleed-out etc.
对弧不良、钢水温度高、拉速快是造成裂纹漏钢的主要原因；
The most reason of cracking breakout is badness of arc and high temperature of molten steel and high withdrawal speed.
本文主要介绍了唐钢薄板坯连铸机结晶器漏钢预报系统的功能算法。
This paper mainly introduces the mould breakout detection system function arithmetic of thin slab caster in Tang Steel.
作为漏钢预报核心技术的模型是目前技术开发和运用的热点和难点。
As a core technology of breakout prediction system, mathematical model is hot spot and nodus in development and application of the technology.
该系统在预报精度和系统性能等方面均优于宝钢原有的漏钢预报装置。
The forecasting accuracy and system property of this new system are better than those of the existing one.
结晶器系统引进了意大利达涅利公司设计的“漏钢预报”这一先进技术。
The mould system introduced the advanced technology of 'breakout prediction' designed by Danieli Company in Italy.
通过对邯钢CSP连铸机的漏钢形式及原因进行分析，提出了预防措施。
Through the analysis for the reasons and forms of the breakout in Hansteel's CSP caster, We raised the preventive measure.
本文对影响钢包滑动水口漏钢的各种因素进行了分析，并制定了相应的改进措施。
This paper analyzes the factors which influence the breakout of the ladle slide gate, and draws the relevant improvement measures.
众所周知漏钢是连铸生产中最为严重的生产事故，造成巨大的直接和间接经济损失。
It is well known that breakout is the most serious accident in casting, it will cause a huge direct or indirect economic loss.
从而验证了严重的结晶器磨损是连铸坯产生偏角区内裂纹乃至漏钢事故的重要原因之一。
These results verify that the severe mold wear is one of the most important reasons that induce the internal crack and even the breakout at the off-corner of billet.
对板坯连铸机产生的纵裂漏钢原因进行了分析，通过制订改进措施，取得了较好的效果。
The reason for longitudinal-crack steel leak is analyzed, some measures formed, better result got.
剖析了连铸结晶器粘结性漏钢的基本特征，利用热电偶，提出一种新的漏钢诊断预报模型。
The basic feature cohesiveness steel leakage of crystallizer in continuos casting process is analyzed. By using thermocouples, a new model of steel leakage diagnosis forecast is stated.
非常适合于引锭头与结晶器铜板之间无规则缝隙的密封，防止开浇时渗、漏钢的现象的出现。
It is ideal for sealing all the random gaps between dummy bar head and mould copper plate, to prevent the hot metal infiltration and break out while casting.
对济钢大板坯连铸机出现的粘结漏钢进行了分析，并提出相应的改进和预防措施，取得了良好效果。
On the basis of the cause analysis of the breakout accident improvement and counter measures are accordingly put forward and good results achieved.
对涟钢CSP连铸机各种形式漏钢的原因进行了较详细的分析，并提出了预防漏钢需采取的有关措施。
The causes of all kinds of breakout for CSP continuous caster in Liangang were analyzed. Moreover the concerned measures preventing breakout were proposed.
提出通过拉坯阻力的实测值与预测值的差值预报拉坯阻力异常和漏钢的新方法，模拟结果表明此法可行。
A new method of predicting breakout and abnormal mould friction by the difference between measured value and predicted value is put forward. The result shows that the way is feasible.
通过分析涟钢过程中的瞬间参数，找出了漏钢的主要原因，即中间包温度过高、拉速过大以及操作不当等。
By analyzing the instantaneous parameters of molten steel leakage during continuous casting at Lianyuan steel, main reasons to cause the leakage were found.
以涟钢CSP薄板坯连铸机为例，对薄板坯连铸机漏钢预报系统的组成、功能及其软件平台作了简要介绍。
Take CSP slab continuous caster of Liangang for example, the structure, system functions and software platforms of breakout prediction system for the slab continuous caster were briefly introduced.
介绍了连铸粘结性漏钢产生的机理和过程，以及宝钢利用人工神经网络技术建立的一套新的漏钢预报系统。
This article presents the mechanism and process of sticking breakout occurring, as well as the newly built prediction system for sticking breakout in Baosteel based on neural network technology.
本文就实际生产中出现的连铸漏钢事故，从操作、设备、工艺三方面进行了一些分析探讨并提出解决的对策。
Based on an analysis of the out-breaking cases met in practical production, measures of preventing the accident are proposeding terms of the operation, equipment and process variables.
针对小方坯连铸高效化改造后拉漏率高的问题 ，分析了造成漏钢的原因 ，介绍了所采取的对策及取得的效果。
The reasons of continuous caster leaking are analyzed aiming to the problem of high leaking rate after reforming the small billet cast to improve its efficiency.
应用结晶器非正弦振动技术可以降低结晶器摩擦阻力，减少粘结性漏钢，同时大幅度降低高拉速时的结晶器振动频率。
The non-sinuous oscillation of the mold is used to reduce the mold friction force and stick type breakout, and to lower the oscillation frequency for high speed casting.
分析了薄板坯连续出现的表面凹陷缺陷，指出如不能及时发现薄板坯的表面凹陷，则会造成漏钢事故，严重制约生产。
The surface indentations frequently occurred on thin slab is analyzed. It is pointed out that they can bring about steel leak and affect production if not being found in time.
结合邯钢三炼钢厂生产实践，分析了工艺、操作和设备等因素对粘结漏钢的影响；提出了降低粘结漏钢次数的主要措施。
The corresponding causes of sticking breakout has been discussed from process, operation and equipment point of view in accordance with production practice in No. 3 steel making plant of Handan steel.