与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
在上面概述的方法之后将产生显示出良好强度和伸长率的细晶粒、完全再结晶、模压淬火的产品。
Following the method outlined above will produce a fine-grained, fully recrystallized, press quenched product that demonstrates good strength and elongation.
本发明的另一个目的是提供具有提高的挤压生产率和良好的机械性能和机械加工性能的模压淬火合金。
Another object of the present invention is to provide a press quench alloy with enhanced extrusion productivity and good mechanical properties and machinability.
结果表明，随着淬火温度的降低，双相钢的屈服和抗拉强度下降，同时总伸长率提高；
The results showed that the tensile strength and yield strength decrease while total elongation increases with decreasing quenching temperature.
锰含量提高并选取合适的淬火温度后，残余奥氏体含量及稳定性提高，抗拉强度显著提升的同时保持了较高的伸长率。
The content and stability of retained austenite is higher after more Mn is added, and also the strength is higher with preferable elongation when the appropriate quenching temperature is chose.
锰含量提高并选取合适的淬火温度后，残余奥氏体含量及稳定性提高，抗拉强度显著提升的同时保持了较高的伸长率。
The content and stability of retained austenite is higher after more Mn is added, and also the strength is higher with preferable elongation when the appropriate quenching temperature is chose.