着重对浇注料的抗渣性进行了讨论。
The emphasis of discussion lies in slag resistance of castable.
也有包由浇注料代替耐火砖砌筑）。
There are also ladles with a concrete lining instead of brick lining.
介绍一种新型浇注料预制块。
优化浇注料，开发喷补料，提高通铁量。
Optimizing Castable Materials, Developing Gunning Material, Raising Iron Influx.
采用坩埚法研究了镁锆质浇注料的抗渣性。
The slag resistance of magnesia - zircon castable was investigated by crucible test.
浇注料的流变性和流动性有较好的相关性。
There is good relevance between the rheology and flow ability.
主要探讨了镁锆质浇注料抗渣渗透性机理。
The mechanism of slag penetration resistance was emphatically studied in this work.
本文介绍了水泥窑用耐火浇注料的研究和应用情况。
The development and application results of refractory castable for cement kiln have been introduced.
研究了锆英石微粉对镁质浇注料结构及性能的影响。
The effect of zircon micropower on the structure and properties of magnesia castable were studied.
蓝晶石加入量为4- 5%时浇注料的性能较好。
When the adding amount of kyanite is 4-5%, the castable performance is better.
因此，GTO可作为硅溶胶结合浇注料的高效减水剂。
This proves that GTO can be used as an excellent dispersant for silica sol-bonded castables.
研究了基质组成对低水泥浇注料高温荷重软化温度的影响。
This article studies the effect of matrix component on refractoriness under load (RUL) of low cement castables.
介绍了户外环氧树脂浇注料的研制和应用，给出了试验结果。
The development and application of outdoor cast material of epoxide resin are introduced. The test results are presented.
这些都与尖晶石熟料及铝—尖晶石浇注料的抗渣性有密切关系。
All of them influence the slag resistances of spinel clinker and its castable refractory.
加入镁铝尖晶石的镁质浇注料在强度方面要好于加入铬矿砂的；
The strength of castable containing MA spinel was better than that of the one contaning chrome ore.
实验证明，镁锆铬质浇注料的抗渣侵蚀能力、抗渣渗透能力较高。
The experiment results show that the resistance of magnesia-zircon-chrome castable to corrosion and penetration of slag are higher.
介绍了不锈钢纤维耐火浇注料在锅炉反射拱上的应用及其经济效益。
Application of stainless steel fibre reinforced castable in boiler reflecting arch and the economical benefits have been introduced.
通过一系列实验室试验，垫补浇注料可认为是较好的罐底耐火材料。
Through a series of laboratory experiment, padding castable is considered to be good as refractory for the ladle bottom.
优化实验后，制备出系列高性能高尔夫球型高铝空心球保温浇注料。
After the optimization of experiment, the golf-shaped bubble bauxite insulating castables with high performance were prepared.
根据感应体熔沟的工作条件提出了感应体熔沟浇注料应满足的要求。
The requirements which inductor refractories should meet were pointed out according to the working conditions of inductor.
中档镁砂粉的添加使浇注料高温处理后的线变化率增大和气孔率增加。
Adding middle grade sintered magnesia powder can enlarge the line ratio and porosity after high temperature treatment.
通过对加热炉水冷梁使用条件的分析，提出了该类浇注料应具有的特点。
The characteristic of castable refractory was advanced by analyzing the service conditions on Water-cooled Beam of heating furnace in this paper.
当尖晶石加入量为15%时，浇注料具有最佳的高温强度和综合抗渣性能。
When the ma spinel addition is 15%, the castable has optimal high temperature strength and slag resistance.
用静态坩埚法研究了加入不同添加剂的刚玉-尖晶石浇注料抗渣侵蚀行为。
The corrosion behaviors of the different additions to corundum-spinel castable refractory were studied by using static crucible method.
重点介绍对用后钢包浇注料的回收工艺及回收物料在高炉铁口炮泥中的应用。
The process of recovery of refractories for ladle and the application of recovery material in blast furnace tap hole clay are introduced emphatically.
本文介绍了粘土结合浇注料的热过程特性和PV C张缝板的研制及其放置方法。
In this paper the characteristic of thermal process of clay castable refractories, the development of PVC expansion crack plate and its installment are introduced.
本次试验以烧结镁砂为主原料，加入铬绿微粉，从而制备出多种配方的镁铬质浇注料。
A variety of chromium-magnesium-containing casting materials for furnace lings were fabricated by adding chrome powder to magnesia-base reactory materials.
基质中同时引入7%的堇青石、7%的焦宝石和2%的石英砂时，浇注料的抗热震性最好。
Adding 7% cordierite, 7% flint clay and 2% quartz sand in matrix enabled the castable to have highest thermal shock resistance.
基质中同时引入7%的堇青石、7%的焦宝石和2%的石英砂时，浇注料的抗热震性最好。
Adding 7% cordierite, 7% flint clay and 2% quartz sand in matrix enabled the castable to have highest thermal shock resistance.