研究石墨直径对等温淬火球铁(adi)水脆化的影响。
The effect of graphite nodule diameter on the water embrittlement of austempered ductile irons (ADI) was investigated.
试样表面镀锡使ADI的抗拉强度和伸长率下降，镀锡层不能有效防止ADI的水脆化。
Soldering on ADI surface decreased the ADI tensile strength and elongation, and solder coating could not prevent from water embrittlement.
聚乙烯涂覆能降低adi的水脆化程度，而环氧树脂和尼龙涂覆无防止ADI水脆化的效果。
Polyethylene coating reduced the degree of ADI water embrittlement, but nylon or epoxy coatings had no effect on ADI water embrittlement prevention.
ADI水脆化是由于水分解的氢使adi基体组织中的应力诱变产生马氏体引起氢脆而导致的。
ADI water embrittlement was attributed to the decomposed hydrogen originated from water, resulting in hydrogen embrittlement of stress induced martensite in ADI matrix.
ADI水脆化是由于水分解的氢使adi基体组织中的应力诱变产生马氏体引起氢脆而导致的。
ADI water embrittlement was attributed to the decomposed hydrogen originated from water, resulting in hydrogen embrittlement of stress induced martensite in ADI matrix.