研究了磷酸盐、含钙材料对水玻璃—矿渣水泥的凝结时间的影响。
This paper studies the influence of phosphate, calcareous material on set time of water glass-slag cement.
结果表明，矿渣细粉对水泥标准稠度需水量基本没有影响，但延长了水泥的凝结时间。
The results showed that the ultrafine slag did almost not influence the needed water of cement, but it postponed the setting time.
研究结果表明，二水石膏对不同窑型水泥的凝结时间的影响类似，对立窑熟料的敏感性要大于回转窑熟料。
The results show that effect of gypsum on the setting time of different cements is similar and shaft kiln clinker is sensitive to gypsum larger than rotary kiln clinker.
结果表明，加入SAE使水泥砂浆的表观密度降低，吸水率下降，并且明显延缓了水泥的凝结时间及水化速度。
The results show that the SAE copolymer emulsion not only reduce the apparent density and absorb water rate of cement mortar, but significantly retard the setting and the hydration of portland cement.
通过选用柠檬酸、白糖、葡萄糖酸钠为矿渣硅酸盐水泥的缓凝剂，测定了不同温度下水泥的凝结时间，分析了温度对混凝土缓凝剂最优掺量的影响规律。
The cement setting time at different temperatures has been measured through choosing citric acid, sugar and sodium gluconate as the retarders of iron Portland cement.
介绍了石膏含量对含钡铁铝酸盐水泥的水化、抗压强度和凝结时间等性能的影响。
The effect of gypsum content on the hydration, compressive strength and setting time of Ba-bearing aluminoferriate cement was presented.
介绍了细水泥浆液及其结石的物理力学特性（粘度、稳定性、凝结时间、抗压和抗渗强度等）的改性研究成果。
The study results on mechanical properties of fine cement grout and its calculus, including cohesion, stability, setting time, compressive resistance and impervious strength, etc.
研究了矿渣、粉煤灰和烧页岩单掺及复掺对高阿利特水泥凝结时间、抗压强度、电阻率、水化产物组成及微观结构的影响。
The effect of slag, fly ash, and calcined shale on setting time, compressive strength, resistivity, composition and microstructure of hydrated product of alite-rich Portland cement were studied.
研究了不同掺量、不同细度的几种粉煤灰对水泥凝结时间的影响。
The effect of several fly ash with different amount and fineness on the setting time of cement is studied.
上述外加剂对砂浆强度和水泥凝结时间的影响也是本研究的部分内容。
Effect of the above admixtures on strength of mortars and setting of cement paste were measured.
试验结果表明，水玻璃能显著加快水泥浆的凝结时间。
The results showed that silicate can significantly speed up the setting time of cement grout.
考察了SAE对水泥砂浆的密度、吸水性、凝结时间以及水泥水化速度的影响。
The effects of SAE on the density, absorbency, setting time and cement hydration of cement mortars were studied.
结果表明，三元复合缓蚀剂具有良好的缓蚀效果且不会对水泥凝结时间和强度产生不良影响。
The results show that composite inhibitors have excellent corrosion inhibition efficiency and won't give bad effect on cement setting time , flexural strength and compressive strength.
阐述了水泥中不可忽视的一项重要技术指标- 凝结时间。
The paper elucidates that for cement an important technical index-setting time, which must not be neglected.
固化磷石膏磨制的水泥和天然二水石膏磨制水泥相比，二者的凝结时间最接近，强度有一定的提高。
Cement prepared with solidified phosphogypsum as retarder had similar setting time as cement prepared with natural gypsum and higher strength than them.
对注浆加固公路路基用的水泥浆体从稳定性、流动度、粘滞度、凝结时间、析水率等方面进行了研究。
In this paper, the behavior of grouting cement mortar to reinforce highway subgrade is analyzed from the aspects of stability, fluidity, viscosity, bleeding ratio and setting time of cement mortar.
结果表明：石灰石的加入，提高了高沸石水泥的早期强度，降低了水泥的标准稠度、凝结时间及干缩率。
It has been shown that limestone can reduce drying shrinkage, standard consistency and setting time of high zeolite cement.
碱磷渣胶凝材料的凝结时间较短，但都可以达到硅酸盐水泥标准。
The setting time of alkali-activated phosphor slag cement is short, but they all adjust to the standards of Portland cement.
混凝土﹑水泥砂浆﹑环氧树脂砂浆的凝结硬化时间长短对测试结果有比较显著的影响。
However, the setting and hardening time of the concrete, the mortar influences the test results obviously.
论文分别研究了木钙、糖钙、酒石酸、焦磷酸钠和蔗糖共五种常用缓凝剂对水泥净浆凝结时间、混凝土凝结时间及强度的影响。
The effects of five common set-retarders on setting time of cement paste and concrete and strength of concrete are studied.
分析了水泥浆液中掺入水玻璃对水泥凝结时间和无侧限抗压强度的影响。
The paper analyzed the influence of cement-silicate on setting time and compressive strength.
凝结时间则由复合体中占比例较多的一种水泥所控制。
Its setting time is determined by the cement which is the majority in this compound cement.
研究了当水泥中混入隔热防水粉后 ，隔热防水粉对水泥标准稠度用水量、凝结时间及体积安定性的影响 。
The effect of the amount of water needed under the cements normal consistency, setting time and volume stability were investigated when heat insulation and waterproofing powder was added in cement.
本标准规定了水泥标准稠度用水量、凝结时间和由游离氧化钙造成的体积安定性的检验方法。
This standard specified the testing methods of water requirement of normal consistency, setting time as well as soundness of portland cements caused by free calcium oxide.
结果表明：钢渣的掺入可以改善水泥浆体的流动性，凝结时间随钢渣掺量增加而延长。
The results show that mobility of cement paste was improved after adding steel slag and setting time extends with the addition of steel slag increasing.
研究了影响碱-粉煤灰-碱矿渣水泥(AAFSC)的强度的因素。测定了其凝结时间。
The influence factors of Alkali - activated - Fly ash - Slag cement (AAFSC) on strength were investigated and the setting time of AASFC was determined.
适当细磨可以缩短含氟立窑水泥配制混凝土的凝结时间，但无法消除立窑水泥配制混凝土凝结时间偏长的缺点。
Finer grinding in a proper way will reduce the setting time of concrete made by shaft kiln cement containing F. However, it is impossible to...
将活化煤矸石掺入硅酸盐水泥中，水泥凝结时间延长，胶砂强度随着活化煤矸石掺量的增加而降低；
The setting time of portland cement was extended with the content of the activated coal gangue increasing. And mechanical properties decreased with the increase content of coal gangue;
将活化煤矸石掺入硅酸盐水泥中，水泥凝结时间延长，胶砂强度随着活化煤矸石掺量的增加而降低；
The setting time of portland cement was extended with the content of the activated coal gangue increasing. And mechanical properties decreased with the increase content of coal gangue;