研究了浸入式水口堵塞的形成机理。
The forming mechanism of the submerged nozzle clogging is investigated.
同时给出了防止水口堵塞的技术措施。
Meanwhile, the measure of preventing nozzle from clogging is presented.
简要叙述了中间包水口堵塞的类型及其特征；
The types and characteristics of clogging of tundish nozzle were briefly introduced.
本文对主要影响连铸中间罐水口堵塞的原因进行了数据统计的工艺分析。
This paper made a data statistic and technologic analysis for the causes of inducing nozzle clogging in tundish of CC.
连铸优质硬线钢小方坯时，铸坯夹渣、水口堵塞等问题影响质量和生产。
The high carbon grade billet cast with continuous caster was influenced by billet inclusion, clogging of the nozzle etc.
连铸水口堵塞的类型有四种，即脱氧产物、固态钢、复杂氧化物及反应产物。
There are four types of the cloggings in the submerged nozzle for continuous casting. They are, namely, deoxidation products, solidified steel, complex oxides and reaction products.
对中间包水口堵塞进行了分析，讨论了为减少水口堵塞和提高钢质量而采取的对策。
Water nozzle clogging of tundish is analyzed, and in order to reduce water nozzle clogging and improve the quality of steel, countermeasure is discussed.
由此分析得出，钢水金属冷凝、连铸保护浇铸不好和钢水不洁净是造成水口堵塞的主要原因。
According to above analysis results, the clogging of submerged nozzle is attributed to molten steel condensation, bad protecting casting and inclusions in molten steel.
中薄板坯连铸机生产低碳高铝钢过程中，浸入式水口堵塞的主要原因是水口与钢水之间产生化学作用和钢水中的氧化铝夹杂物在水口壁上沉积。
The main reason that the submerged nozzle clogged during continuous casting of high aluminum low carbon steel is aluminate that aggraded the submerged nozzle wall.
铝锰铁复合脱氧剂脱氧与铝铁脱氧比较，可提高铝的利用率，降低钢中氧、氮气体及夹杂物含量，有利于减少连铸水口堵塞，提高钢液的纯净度。
The result indicated that the Al - Mn- Fe alloy deoxidant can increase utilization ration of aluminum, decrease content of oxygen and nitrogen and inclusion in the steel.
所有流下下水口的液态脂肪很有可能会缓缓堵塞下水管的流量。
All that liquid fat running down the plughole will probably be slowly constricting the drain of your sink.
堵塞沉积主要是由于氧化物颗粒附着到浸入式水口耐火材料的内表面，继而烧结在一起所致。
The clogging deposit is mainly due to the attachment of oxide particles onto the inner surface of the submerged nozzle refractory followed by sintering.
通过室内试验，研究地下滴灌滴头负压堵塞与滴头出水口形式、滴头流量间的关系，发现滴头出水口形式对滴头抗堵塞性能影响显著。
The results of the experiment indicated that the outlet form of emitters affected the anti-clogging performance of negative pressure more than the flow rate of emitters.
结果表明，提高喂线速度、加大喂线量和增加水口内径可避免水口的堵塞。
The results showed that increasing the feeding speed, the amount of Ca-Fe cored wire and the diameter of the tundish nozzle can prevent blockage.
水闸门不能处理排水口的积水，部分是由于沉降堵塞。
The sluice gates were not able to handle the overflow of water, partially due to sedimentation blockage.
室外排水口在冰冻气温下可能会冻结并堵塞排水管。
Outdoor drains are subject to freezing temperatures which can obstruct the drain line.
另外，由于灌水器进口处结构设计不合理，进水口段发生堵塞的几率也很大。
Furthermore, because of the improper structure of the emitter's inlets, the probability of clogging in inlets is also great.
由于生产轴承钢水口的堵塞，严重影响生产的顺利进行。
The bearing steel production is delayed by the submerged nozzle clogging.
由于生产轴承钢水口的堵塞，严重影响生产的顺利进行。
The bearing steel production is delayed by the submerged nozzle clogging.