蒙乃尔400目免疫氯离子应力腐蚀开裂在典型环境。
Monel 400 mesh is immune to chloride ion stress corrosion cracking in typical environments.
结果表明，不锈钢盘管失效的原因是氯离子引起的应力腐蚀开裂所致。
The result indicated that the failure cause of the stainless steel spiral pipe is the stress corrosion crack induced by Cl- ion.
结果表明，介质中所含的微量氯离子引起的晶间型应力腐蚀开裂导致再沸器失效。
The result showed that the direct reason of reboiler invalidation was the intercrystalline stress corrosion and crack caused by micro-chloride in the medium.
结果表明，黄铜管的开裂为氯离子引起的穿晶应力腐蚀开裂；
The results showed that it was chlorine ion that resulted in transgranular stress corrosion cracking in brass tubes.
结果表明，紫铜管渗漏系腐蚀引发裂纹所致，而涂在铜管表面的油胶中的氯离子是引起紫铜管应力腐蚀开裂的主要因素。
It was concluded that the cl ion in the oil glue resulted in stress corrosion cracking of the pure copper tube.
结果表明，紫铜管渗漏系腐蚀引发裂纹所致，而涂在铜管表面的油胶中的氯离子是引起紫铜管应力腐蚀开裂的主要因素。
Cl ion was also found in oil glue by chemical analysis method. It was concluded that the cl ion in the oil glue resulted in stress corrosion cracking of the pure copper tube.
结果表明，紫铜管渗漏系腐蚀引发裂纹所致，而涂在铜管表面的油胶中的氯离子是引起紫铜管应力腐蚀开裂的主要因素。
Cl ion was also found in oil glue by chemical analysis method. It was concluded that the cl ion in the oil glue resulted in stress corrosion cracking of the pure copper tube.