某公司的立式氨冷凝器波纹换热管采用316L不锈钢制造，使用1年后陆续发生腐蚀穿孔现象。
The recuperator tube of ammonia condenser on a factory was made of 316l stainless steel and pitted after used for only one year.
介绍了酮苯装置立式氨用冷凝器的失效情况，确定了海水局部腐蚀是冷凝器失效的主要原因。
The corrosion failure of vertical ammonia-seawater condenser used in acetone-benzol plant was introduced. It is determined that the main failure reason is caused by seawater local corrosion.