结果表明氧化铝纤维与硅相之间存在共格界面，可作为硅相非自发形核的衬底；
The results indicate that there is a coupled interface between alumina fiber and Si phase, and the fiber can serve as propitious sites for the heterogenous nucleation of Si phase.
利用挤压铸造制备了氧化铝纤维增强铝硅合金复合材料，研究了这种材料的界面对其耐磨性的影响。
A alumina short fibre reinforced aluminum silicon alloy composite is manufactured by squeeze casting. The effect of the composite's interface on its wear resistance is studied.
以柠檬酸、乳酸及金属盐为原料，采用有机凝胶法制备了微细金属镍纤维、氧化镁纤维和氧化铝纤维。
Metallic nickel and ceramic alumina, magnesia fibres were prepared respectively by the organic-gel method from the raw materials of citric or lactic acid and the their metal salts.
利用挤压铸造制备了氧化铝纤维增强锌合金复合材料，研究了氧化铝纤维对锌合金复合材料凝固组织的影响。
Alumina fiber reinforced zinc alloy composites were manufactured by squeeze casting, and the effects of alumina fibers on the solidified structures of the zinc alloy composites were studied.
含锆型硅酸铝耐火纤维棉，以高纯氧化铝硅石粉及锆英沙合成为原料，经电阻炉熔融喷吹或甩丝成纤工艺生产而成。
ZA Swinging Fibre, abopting HP Alumina. Silica Powder, Zirconia as the material, melted by Resistance Furnace, blowing or swinging, is produced by swinging technology.
介绍了铝氧化反应结合技术与干湿法纺丝工艺相结合制备氧化铝中空纤维膜的方法。
The preparation method of alumina hollow fiber membrane by reaction bonding of aluminum oxide (RBAO) technique combined with dry wet spinning process was introduced in this paper.
本文利用介孔碳的软模板合成方法和阳极氧化铝膜的孔道限域性制备有序的介孔碳纳米纤维。
Ordered mesoporous carbon nanofibers were prepared by combining the soft template synthesis method of mesoporous carbons with the confinement of channels of anode alumina membranes.
本文在国产氧化铝短纤维基础上，研究了氧化铝短纤维增强铝硅合金复合材料的凝固组织。
In this paper, the solidifying structure of alumina short fiber reinforced aluminum-silicon alloy composite is studied on the basis of domestic alumina short fibers.
由本发明制备的氧化铝纳米纤维有着广泛的应用前景，可以用作陶瓷材料、隔热材料以及其它潜在的功能材料等。
The nano aluminum oxide fiber has wide application and may be used as ceramic material, heat isolating material, latent functional material, etc.
介孔分子筛纤维的直径和长度分别对应于阳极氧化铝膜的孔径和厚度。
The diameter and length of mesoporous fibers is corresponding to pore diameter and thickness of AAO membrane.
这些具有多级有序结构的纤维可以非常方便地用表面活性剂作为结构导向剂，用阳极氧化铝膜作为硬模板来制备。
These fibers with hierarchical organization can easily be prepared using surfactants as structure-directing agent and anodic aluminium oxide (AAO) membranes as hard template.
试验结果表明，氧化铝短纤维预制件的抗压强度随着纤维体积分数的升高而升高，随着黏结剂质量分数的提高而升高。
The experimental results show that the compressive strength of preform increases with the increasing of fiber volume fraction and binder mass fraction.
用挤压铸造法制备了氧化铝短纤维增强铝合金内燃机活塞。
Al2O3 short fiber reinforced aluminum matrix composites for high performance piston was prepared by squeezing casting.
◎高纯陶瓷纤维甩丝棉是通过电熔氧化铝和二氧化硅混合料，甩丝成纤工艺生产而成；
Huolong Ceramic Fiber Blown Bulk was processed by the blown work on the electric melting ore.
ASPA - 1型和aspa - 2型的氧化铝—氧化硅纤维纸是优质的轻质耐火材料，它们由高纯度的氧化铝—氧化硅纤维制造成高弹性的薄片状的。
Types ASPA-1 and ASPA-2 alumina-silica fiber paper are premium grade lightweight refractory material made from high-purity alumina-silica fibers formed into highly flexible sheets.
ASPA - 1型和aspa - 2型的氧化铝—氧化硅纤维纸是优质的轻质耐火材料，它们由高纯度的氧化铝—氧化硅纤维制造成高弹性的薄片状的。
Types ASPA-1 and ASPA-2 alumina-silica fiber paper are premium grade lightweight refractory material made from high-purity alumina-silica fibers formed into highly flexible sheets.